Aqueous pigment dispersion and aqueous ink

ABSTRACT

The present invention provides an aqueous pigment dispersion including a pigment, an anionic group-containing organic polymer compound, and bio-nanofibers having an average diameter of 1 nm or more and 100 nm or less and an aspect ratio of 100 or more, and also provides an aqueous ink using the aqueous pigment dispersion. The bio-nanofibers are preferably cellulose nanofibers or chitosan nanofibers. The anionic group-containing organic polymer compound is preferably at least one selected from the group consisting of acrylic resins having anionic groups, polyurethane resins having anionic groups, and polysaccharide derivatives having anionic groups.

TECHNICAL FIELD

The present invention relates to an aqueous pigment dispersion or the like containing bio-nanofibers and a method for producing the same.

BACKGROUND ART

In recent years, an aqueous ink composition (may be referred to as an “aqueous ink” hereinafter) has taken the place of an organic solvent-based ink in a wide range of fields because of its safety and little environmental load, and particularly an odorless aqueous ink has become essential as an ink which can be used even in a closed space such as an office or the like.

The aqueous ink is applied to various printing methods such as an offset printing method, a gravure printing method, an ink jet recording method, and the like. In particular, the ink jet recording method is capable of on-demand printing and is thus currently often investigated for the purpose of replacing an electrophotographic (toner) method used in offices and the like.

The physical properties required for an aqueous ink using an ink jet recording method include both the color development (optical density) and rubfastness of a formed image. For this requirement, there is known a two-liquid reaction system using an image forming ink and a fixing ink (also referred to as a “treatment agent”) (for example, refer to Patent Literatures 1 to 3). However, in the case of the two-liquid reaction system, printing is actually performed in two steps using the image forming ink and the fixing ink, and thus it is difficult to realize high-speed printing at a level equal or higher than the electrophotographic (toner) method.

On the other hand, bio-nanofibers are produced by uniformly refining (forming nanofibers) cellulose or chitin/chitosan at a nano-level and, in an industrial application, bio-nanofibers are known to be added for the purpose of improving the drying properties and toughness of coating films by imparting thixotropic viscosity to aqueous emulsion compositions for coat bonding and filling (for example, refer to Patent Literature 4), and added to a pigment composition for the purpose of imparting good rheology characteristics (for example, refer to Patent Literature 5). However, there has not been known an example of use for the purpose of improving the optical density and rubfastness of an aqueous ink.

An aqueous ink for writing implements is known, in which an aqueous ink is mixed with modified cellulose nanofibers characterized by a complex structure in order to secure excellent dispersion stability even of a coloring agent with high specific gravity (for example, refer to Patent Literature 6). The modified cellulose nanofibers described in Patent Literature 6 have a predetermined cellulose crystal structure and are required to be subjected to reduction reaction to adjust a content of carboxyl groups and a total content of aldehyde groups and ketone groups after selective oxidation of hydroxyl groups at specified positions in a cellulose molecule. Therefore, there is the problem of high cost and a large chemical limit of ink composition design.

CITATION LIST Patent Literature

PTL 1: Japanese Unexamined Patent Application Publication No. 2013-35227

PTL 2: Japanese Unexamined Patent Application Publication No. 2013-35226

PTL 3: Japanese Unexamined Patent Application Publication No. 2011-140213

PTL 4: Japanese Unexamined Patent Application Publication No. 10-95922

PTL 5: Japanese Unexamined Patent Application Publication (Translation of PCT Application) No. 2013-527876

PTL 6: Japanese Unexamined Patent Application Publication No. 2013-181167

SUMMARY OF INVENTION Technical Problem

An object of the present invention is to provide an aqueous pigment dispersion being excellent in optical density and rubfastness of a resultant image and provide an aqueous ink.

Solution to Problem

As a result of earnest research, the inventors found that the problems described above can be solved by an aqueous pigment dispersion and an aqueous ink each containing, as essential components, bio-nanofibers having a specified average particle diameter and aspect ratio and an anionic group-containing organic polymer compound functioning as a pigment dispersant and a binder.

That is, the present invention provides an aqueous pigment dispersion containing at least a pigment, an anionic group-containing organic polymer compound, and bio-nanofibers having an average diameter (fiber diameter) of 1 nm or more and 100 nm or less and an aspect ratio of 100 or more, and also provides an aqueous ink using the aqueous pigment dispersion.

Further, present invention provides a method for producing the aqueous pigment dispersion and the aqueous ink.

Advantageous Effects of Invention

According to the present invention, it is possible to provide an aqueous pigment dispersion being excellent in optical density and rubfastness of a resultant image and to provide an aqueous ink using the aqueous pigment dispersion.

DESCRIPTION OF EMBODIMENTS (Pigment)

A pigment used in the present invention is at least one pigment selected from known common organic pigments or inorganic pigments. Also, the present invention can use either an untreated pigment or a treated pigment. The treated pigment includes a so-called self-dispersion type pigment. This is because the self-dispersion type pigment is produced by, for example, bonding (grafting) hydrophilic groups on the surfaces of a pigment through physical treatment or chemical treatment of the pigment.

The self-dispersion type pigment represents a pigment which can be dispersed or dissolved in an aqueous medium without a dispersant. The expression “dispersed or dissolved in an aqueous medium without a dispersant” represents a state of being stably present in an aqueous medium due to hydrophilic groups of the surfaces even without using a dispersant for dispersing the pigment. The expression “stably present in an aqueous medium” represents being stable (change in pigment particle diameter within +/−30%) for 90 days in water (25° C., solid content of 10% by mass) without a dispersant.

The hydrophilic group is preferably one or more hydrophilic groups selected from the group consisting of —OM, —COOM, —SO₃M, —SO₂M, —SO₂NH₂, —RSO₂M, —PO₃HM, —PO₃M₂, —SO₂NHCOR, —NH₃, and —NR₃, that is, an anionic hydrophilic functional group. In these formulae, M each independently represent a hydrogen atom, an alkali metal, ammonium, a phenyl group or organic ammonium which may have a substituent. In these formulae, R each independently represent an alkyl group having 1 to 12 carbon atoms or a naphthyl group which may have a substituent.

Examples of the self-dispersion type pigment which can be used include pigments treated by methods described in Japanese Unexamined Patent Application Publication No. 8-3498, Japanese Unexamined Patent Application Publication (Translation of PCT Application) No. 2000-513396, Japanese Unexamined Patent Application Publication (Translation of PCT Application) No. 2008-524400, Japanese Unexamined Patent Application Publication (Translation of PCT Application) No. 2009-515007, Japanese Unexamined Patent Application Publication (Translation of PCT Application) No. 2010-537006, and Japanese Unexamined Patent Application Publication (Translation of PCT Application) No. 2012-500866. Either an inorganic pigment or an organic pigment can be used as a raw material of the self-dispersion type pigment.

In printing using plain paper as a recording material, a yellow ink, a cyan ink, a magenta ink, a black ink, and the like are used alone or as an ink set of combination of plural inks. Pigments used for these inks are not particularly limited, and pigments used for usual aqueous inks can be used. Specifically, a known inorganic pigment and organic pigment which can be dispersed in water or a water-soluble organic solvent can be used. Examples of the inorganic pigment include iron oxide, carbon black produced by a known method such as a contact method, a furnace method, a thermal method, or the like, and the like. Examples of the organic pigment which can be used include azo pigments (including azo lake pigments, insoluble azo pigments, condensed azo pigments, chelate azo pigments, and the like), polycyclic pigments (for example, phthalocyanine pigments, perylene pigments, perinone pigments, anthraquinone pigments, quinacridone pigments, dioxazine pigments, thioindigo pigments, isoindolinone pigments, quinophthalone pigments, and the like), dye chelates (for example, basic dye-type chelates, acidic dye-type chelates, and the like), nitro pigments, nitroso pigments, aniline black, and the like.

Examples of pigments used as carbon black for black inks include No. 2300, No. 2200B, No. 900, No. 960, No. 980, No. 33, No. 40, No. 45, No. 45L, No. 52, HCF88, MA7, MA8, MA100, and the like, which are manufactured by Mitsubishi Chemical Corporation); Raven 5750, Raven 5250, Raven 5000, Raven 3500, Raven 1255, Raven 700, and the like, which are manufactured by Columbian Chemicals Company); Regal 400R, Regal 330R, Regal 660R, Mogul L, Mogul 700, Monarch 800, Monarch 880, Monarch 900, Monarch 1000, Monarch 1100, Monarch 1300, Monarch 1400, and the like, which are manufactured by Cabot Corporation; Color Black FW1, FW2, FW2V, FW18, FW200, S150, S160, and S170, Printex 35, U, V, and 1400U, Special Black 6, 5, 4, and 4A, NIPEX 150, NIPEX 160, NIPEX 170, NIPEX 180, and the like, which are manufactured by Degussa Corporation.

Examples of pigments used for yellow inks include C. I. Pigment Yellow 1, 2, 12, 13, 14, 16, 17, 73, 74, 75, 83, 93, 95, 97, 98, 109, 110, 114, 120, 128, 129, 138, 150, 151, 154, 155, 174, 180, 185, and the like.

Examples of pigments used for magenta inks include C. I. Pigment Red 5, 7, 12, 48(Ca), 48(Mn), 57(Ca), 57:1, 112, 122, 123, 146, 168, 176, 184, 185, 202, 209, and the like.

Examples of pigments used for cyan inks include C. I. Pigment Blue 1, 2, 3, 15, 15:3, 15:4, 16, 22, 60, 63, 66, and the like.

For example, a commercial product may be used as the self-dispersion type pigment. Examples of the commercial product include “CAB-O-JET 200”, “CAB-O-JET 250C”, “CAB-O-JET 260M”, “CAB-O-JET 270Y”, “CAB-O-JET 300”, “CAB-O-JET 400”, “CAB-O-JET 450C”, “CAB-O-JET 465M”, and “CAB-O-JET 470Y”, which are manufactured by Cabot Specialty Chemicals, Inc.; “BONJET BLACK CW-2” and “BONJET BLACK CW-3” which are manufactured by Orient Chemical Industries Co., Ltd.; “LIOJET WD BLACK 002C” manufactured by Toyo Ink Mfg. Co., Ltd., and the like. Also, a pigment dispersion produced by dispersing the self-dispersion type pigment in an aqueous medium can be used as a commercial product. Examples thereof include “SENSIJJET Black SDP100”, “SENSIJJET Black SDP1000”, “SENSIJJET Black SDP2000”, “Sensijet Ultra Yellow PY74”, “Sensijet Ultra Magenta PR122”, “Sensijet Ultra Cyan PB15:4”, “Sensijet Ultra K”, and the like, which are manufactured by United States, Sensient Colors Inc.

These self-dispersion type pigments may be used alone or in combination of two or more types.

In particular, when an aqueous ink is used for ink jet, the content (mass basis) of a pigment is preferably 0.5% to 30% and more preferably 1.0% to 12% relative to the total amount of the aqueous ink. In order to achieve a sufficient optical density on plain paper, the content is most preferably 3% or more and 12% or less. This is because with the content of less than 3%, a printing density on plain paper cannot be secured, while with the content exceeding 12%, discharge stability of the aqueous ink from an ink jet head is degraded due to an increase in ink viscosity or the like.

The particle diameter of the pigment is preferably 1 μm or less and more preferably 10 nm to 150 nm, and the pigment preferably still more preferably contains particles of 50 nm to 120 nm.

(Bio-Nanofibers)

The bio-nanofibers used in the present invention represent cellulose or chitin/chitosan uniformly refined (nano-fiberized) at a nano-level. Therefore, the bio-nanofibers may be referred to as “biomass-nanofibers” (reference: Japanese Unexamined Patent Application Publication No. 2013-216766, etc.).

Even when the bio-nanofibers used in the present invention contain impurities other than cellulose, chitin, or chitosan, there is no particular hindrance, but cellulose nanofibers or chitosan nanofibers are preferred.

In the specification, the term “nanofibers” represents a fibrous material having a diameter of 1 nm to 100 nm and an aspect ratio (=length/diameter) of 100 or more. Therefore, the “cellulose nanofibers” represents cellulose fibers having a diameter of 1 nm to 100 nm and an aspect ratio (=length/diameter) of 100 or more.

(Cellulose Nanofibers)

The cellulose nanofibers used in the present invention preferably have an average diameter (may be referred to as “fiber diameter”) of 1 nm to 100 nm, more preferably 1 nm to 50 nm, still more preferably 3 nm to 30 nm, and even more preferably about 20 nm. The aspect ratio is preferably 100 or more, more preferably 100 to 10000, and still more preferably 100 to 2000. This is because the range can provide a satisfactory effect at low cost. The cellulose nanofibers can be used alone or as a mixture of two or more types.

The average diameter (short diameter) of the cellulose nanofibers of the present invention defines the average diameter and aspect ratio of the cellulose nanofibers under a dry condition. The “aspect ratio” in the present invention represents a ratio (average fiber length/average diameter) of the average fiber length to the average diameter of the cellulose nanofibers. In the present invention, the average diameter and aspect ratio under a dry condition can be measured by a scanning electron microscope (SEM) or a transmission electron microscope (TEM, with electron staining). For example, a dispersion prepared by dispersing cellulose nanofibers is cast on a substrate and observed with SEM, and diameter and length values of 20 or more fibers per image are read. This is performed for images of at least three regions, which are not overlapped with each other, to obtain information of the diameters and lengths of at least 30 fibers, preferably 100 fibers. The average diameter can be calculated from the date of fiber diameters, and the average fiber length can be calculated from the date of lengths. However, the aspect ratio under a dry condition may be calculated by a method other than the method described above unless the value is changed. In the present invention, the dry condition is a condition in which 99% by mass or more of liquid is removed from at least the cellulose nanofibers by a usual known method such as natural drying or reduced-pressure freeze drying.

The cellulose nanofibers used in the present invention can be expressed by the average diameter (short diameter) and aspect ratio calculated based on the results of electron microscope observation as described above. The cellulose nanofibers can be also expressed by a hydrodynamic particle diameter using a commercial electrical/optical particle diameter measuring apparatus. The hydrodynamic particle diameter of the cellulose nanofibers used in the present invention can be measured by, for example, using dynamic light scattering Nanotrac particle size analyzer UPA-150EX (manufactured by Nikkiso Co., Ltd.). The hydrodynamic particle diameter of the cellulose nanofibers described in the specification corresponds to the average particle diameter of a hydrodynamic equivalent spherical model formed when the cellulose nanofibers are dispersed in a solvent. In principle, a certain volume of particles are sorted in order from smaller ones to display a particle diameter distribution. Thus, the mode value corresponds to the maximum value of the particle diameter distribution. The 20% particle diameter is the particle diameter when particles at a 20% volume in the particle diameter distribution are sorted, and the 80% particle diameter is the particle diameter when particles at a 80% volume in the particle diameter distribution are sorted.

The most frequent value (mode value) of the hydrodynamic particle diameter at 0.1% by mass (solvent:water) of the cellulose nanofibers used in the present invention is preferably 100 nm or more and 800 nm or less, more preferably 200 nm or more and 700 nm or less, and still more preferably 250 nm or more and 650 nm or less. In the hydrodynamic particle diameter distribution, a value of the 80% particle diameter to the 20% particle diameter, that is, a value of (80% particle diameter)/(20% particle diameter), is preferably 10 or less, more preferably 8 or less, and still more preferably 6 or less.

With respect to the cellulose nanofibers used in the present invention, a specific surface area (calculated with ultrasonic dispersion treatment: 1 minute, sample refractive index: 1.56 to 0.00i, dispersion medium refractive index: 1.333 to 0.00i) calculated from a particle size distribution (volume-based particle diameter distribution) measured by a light scattering method is preferably 800 cm²/cm³ or more and 3000 cm²/cm³ or less, more preferably 1000 cm²/cm³ or more and 2800 cm²/cm³ or less, and still more preferably 1200 cm²/cm³ or more and 2600 cm²/cm³ or less. The specific surface area is a total (cm²) of surface areas of particles per unit volume (cm³), but it is a value calculated from particle diameter distribution data and thus generally does not agree with a specific surface area measured based on another measurement principle.

In the case of an aqueous ink, the content (mass basis) of the cellulose nanofibers used in the present invention is preferably a cellulose nanofiber/pigment ratio of 1/100 to 1/8, more preferably 1/100 to 15/100, still more preferably 1/100 to 14/100, and even more preferably 1/100 to 13/15. This is because within the range, color development (optical density) and rubfastness of the formed image reach a desired level without degrading the adaptability for various printing methods.

Thus, when the content of the cellulose nanofibers in an aqueous pigment dispersion is a specified amount, desired levels of the color development (optical density) and rubfastness of an image formed with the aqueous ink can be achieved. Although the mechanism of this has not been sufficiently examined, it is supposed as follows.

A glucose unit constituting cellulose takes a chair conformation, and thus hydroxyl groups are arranged in a horizontal direction and only C and H are arranged in a vertical direction with respect to a glucopyranose ring. Therefore, the vertical direction of cellulose is hydrophobic, while the horizontal direction is hydrophilic. This tendency is further enhanced by an increase in surface area due to nano-fiberization. Therefore, in the aqueous ink, in a composite material of pigment particles composed of the cellulose nanofibers with an anionic group-containing organic polymer compound described below, the interfacial tension between the pigment particles and the anionic group-containing organic polymer compound is decreased, and repulsive force is imparted to overcome the Van der Waals force between the pigment particles while controlling the charge on the pigment particle surfaces. It is thus considered that a high degree of balance essential for stable dispersion of the pigment can be achieved.

Therefore, even when printing is performed on plain paper containing various paper components, the pigment particles can be fixed without being unnecessarily penetrated into the paper used as an object to be printed, thereby exhibiting a high optical density, causing no color mixing of color inks adjacent to each other in multicolor-type color printing, and causing excellent rubfastness.

In the case of the aqueous ink, particularly for ink jet”, the content of the cellulose nanofibers is preferably in a range of 0.001% to 3%, more preferably 0.01% to 2%, and still more preferably 0.05% to 1% relative to the total ink mass. This is because with the content of less than 0.001%, the optical density and rubfastness cannot be secured, while with the content exceeding 3%, printability is impaired due to an increase in ink viscosity or the like.

The cellulose nanofibers used in the present invention are not particularly limited and a commercial product or a product produced by a known production method can be used. The cellulose nanofibers are generally produced by fibrillating or refining a cellulose fiber-containing material by grinding and/or beating using a refiner, a high-pressure homogenizer, a medium stirring mill, a millstone, a grinder, or the like, and for example, can be produced by a known method such as a method described in Japanese Unexamined Patent Application Publication No. 2005-42283. Also, microorganisms (for example, acetobacter) can be used for production. Further, a commercial product can be used. Examples of the cellulose fiber-containing material include known materials derived from origins such as plants (for example, wood, bamboo, cotton, jute, kenaf, agricultural residues, cloth, pulp, regenerated pulp, and wastepaper), animals (for example, sea squirt), algaes, microorganisms (for example, acetobacter), microorganism products, and the like. In the present invention, any one of these materials can be used. Among these, cellulose nanofibers derived from plants or microorganisms are preferred, and cellulose nanofibers derived from plants are more preferred.

The cellulose nanofibers used in the present invention need not be so-called modified cellulose nanofibers which are chemically modified in some way as described in Japanese Unexamined Patent Application Publication No. 2013-181167 and Japanese Unexamined Patent Application Publication No. 2010-216021, and so-called unmodified cellulose nanofibers produced by, for example, a method described in Japanese Unexamined Patent Application Publication No. 2011-56456, and an unmodified cellulose nanofiber commercial product can also be used. Examples of the unmodified cellulose nanofiber commercial product include bio-nanofiber “BiNFi-s” series of Sugino Machine Limited, “Celish” series of Daicel FineChem Ltd., and “CNF” series of Chuetsu Pulp & Paper Co., Ltd. These cellulose nanofibers can be used alone or as a mixture of two or more.

In a ¹³C-NMR chart of the cellulose nanofibers used in the present invention, it can be confirmed that a peak at 62 ppm corresponding to the C6-position of a primary hydroxyl group of a glucose unit is present. In the case of modified cellulose nanofibers, for example, when hydroxyl groups at the C6-positions of glucose units in a cellulose molecule are partially converted to carboxyl groups by oxidation or the like, the peak at 62 ppm disappears, and a peak at 178 ppm derived from carboxyl groups is present instead.

The cellulose nanofibers used in the present invention are not modified by oxidation or the like as described above. Therefore, hydroxyl groups of cellulose may be slightly substituted with carboxyl groups by treatment in a process of producing and purifying cellulose nanofibers. However, an amount of substituent generally does not exceed 0.1 mmol/g.

The amount of carboxyl groups can be measured by the following method. First, 60 cm³ of a 0.5% by mass slurry (water dispersion) of cellulose nanofibers is prepared and adjusted to pH 2.5 by adding a 0.1 mol/L aqueous hydrochloric acid solution. Then, electric conductivity is measured until the pH becomes 11 by adding dropwise a 0.05 mol/L aqueous sodium hydroxide solution. The amount of carboxyl groups can be calculated by using a formula below from an amount (a) of sodium hydroxide consumed in a weak acid neutralization step in which the electric conductivity is gently changed.

Carboxyl group amount (mmol/g cellulose nanofibers)=a (cm³)×0.05/cellulose nanofiber mass (g)  [Math. 1]

The thermal decomposition temperature of the cellulose nanofibers used in the present invention depends on the crystallinity, average degree of polymerization, etc. but is generally about 250° C. to 280° C. In the specification, the thermal decomposition temperature represents a temperature at which the weight starts to decrease due to thermal decomposition when the temperature is increased from room temperature (temperature rising speed: 5° C./min) by a thermogravimeter-differential thermal analyzer (TG-DTA). The temperature at which the weight starts to decrease is defined as a temperature at an intersect of a tangent at the time of large weight decrease and a tangent before weight decrease in a graph in which the weight decrease rate is plotted on the ordinate, and the temperature is plotted on the abscissa.

The degree of crystallization (ratio of cellulose I-type crystal structure) of the cellulose nanofibers used in the present invention is not particularly limited. The degree of crystallization (ratio of cellulose I-type crystal structure) is determined by X-ray diffraction. For example, the degree of crystallization of type I cellulose can be calculated from X-ray diffraction results by using a method of Segal et al. (L. Segal, J. J. Greely et al, Text. Res. J., 29, 786, 1959) and a method of Kamide et al. (K. Kamide et al, Polymer J., 17, 909, 1985). That is, the degree of crystallization can be calculated by a formula below from the diffraction intensity of a 002 plane at 2θ=22.6° and the diffraction intensity of an amorphous portion at 2θ=18.5° using the diffraction intensities at 2θ=4° to 32° as a baseline in a diffraction chart obtained by X-ray diffraction measurement.

χ_(c)=(I _(002c) −I _(a))/I _(002c)×100  [Math. 2]

(In the formula, χ_(c) represents the degree of crystallization of type I cellulose (%), I_(002c) represents the 002 plane diffraction intensity at 2θ=22.6°, and I_(a) represents the amorphous portion diffraction intensity at 2θ=18.5°.)

The cellulose nanofibers used in the present invention need not be chemically treated by oxidation of cellulose nanofibers and thus need not be improved in resistance to radical an alkali over a long period of time, and it is unnecessary to select cellulose with a high degree of crystallization of type I cellulose (degree of crystallization of about 65% to 85%). That is, the effect of the present invention can be exhibited by using cellulose nanofibers derived from cellulose as a starting material which is produced from wood pulp and which has a degree of crystallization of about 50% to 70% (for example, 55% to 65%).

The crystal form of the cellulose nanofibers used in the present invention is not particularly limited. Both Iα- and Iβ-cellulose can be preferably used as the crystal form of the cellulose nanofibers. Cellulose derived from higher plants such as cotton contains a large amount of Iβ crystal component, while bacterial cellulose contains a large amount of Iα crystal component. Cellulose can be properly selected from an economical viewpoint.

(Chitosan Nanofibers)

The chitosan nanofibers used in the present invention preferably have an average diameter (referred to as a “fiber diameter”) of 1 to 100 nm, more preferably 1 to 50 nm, still more preferably 3 to 30 nm, and even more preferably about 20 nm. The aspect ratio is preferably 100 or more, more preferably 100 to 10,000, and still more preferably 100 to 2000. This is because within the range, a satisfactory effect can be obtained at low cost. The chitosan nanofibers are used singly, used as a mixture of two or more types, or used in combination with the cellulose nanofibers.

The average fiber length, average diameter, etc. of the chitosan nanofibers of the present invention are defined as the same as the average diameter and aspect ratio of the cellulose nanofibers and can be calculated as described above.

The most frequent value (mode value) of the hydrodynamic particle diameter at 0.1% by mass (solvent:water) of the chitosan nanofibers used in the present invention is preferably 100 nm or more 800 nm or less, more preferably 200 nm or more and 700 nm or less, and still more preferably 250 nm or more and 650 nm or less. In the hydrodynamic particle diameter distribution, a ratio value of the 80% particle diameter to the 20% particle diameter, that is, a value of (80% particle diameter)/(20% particle diameter), is preferably 10 or less, more preferably 8 or less, and still more preferably 6 or less.

With respect to the chitosan nanofibers used in the present invention, a specific surface area (calculated with ultrasonic dispersion treatment: 1 minute, sample refractive index: 1.56 to 0.00i, dispersion medium refractive index: 1.333 to 0.00i) calculated from a particle size distribution (volume-based particle diameter distribution) measured by a light scattering method is preferably 800 cm²/cm³ or more and 3,000 cm²/cm³ or less, more preferably 1,000 cm²/cm³ or more and 2,800 cm²/cm³ or less, and still more preferably 1,200 cm²/cm³ or more and 2,600 cm²/cm³ or less. The specific surface area is a total (cm²) of surface areas of particles per unit volume (cm³), but it is a value calculated from particle diameter distribution data and thus generally does not agree with a specific surface area measured based on another measurement principle.

The content (mass basis) of the chitosan nanofibers used in the present invention is preferably a chitosan nanofiber/pigment ratio of 1/100 to 1/8, more preferably 1/100 to 15/100, still more preferably 1/100 to 14/100, and even more preferably 1/100 to 13/100. This is because within the range, color development (optical density) and rubfastness of the formed image reach a desired level without degrading the suitability for various printing methods.

Thus, when the content of the chitosan nanofibers in the aqueous pigment dispersion is a specified amount, desired levels of the color development (optical density) and rubfastness of an image formed with the aqueous ink can be achieved. The mechanism of this has not been sufficiently examined but is supposed as follows.

Chitosan is an aminosaccharide obtained by deacetylating chitin (β-1,4-poly-N-acetyl-D-glucosamine) extracted from crab and shrimp shells and has a structure in which a hydroxyl group at the C2-position of cellulose is substituted by an amino group. Conversion (deacetylation reaction) of chitin to chitosan does not completely proceed, and N-acetylglucosamine is often contained in a portion of a sugar chain. When 70% or more of glucosamine residues are deacetylated, chitin is generally referred to as “chitosan”. Therefore, the quality of chitosan is shown by a deacetylation rate (may be denoted by “% DA”) measured by NMR spectroscopy, infrared absorption spectroscopy (IR), and a colloidal titration method.

A glucose unit constituting chitosan takes a chair conformation, and thus hydroxyl groups are arranged in a horizontal direction and only C and H are arranged in a vertical direction with respect to a glucopyranose ring. Therefore, like in the cellulose nanofibers, the vertical direction of chitosan is hydrophobic, while the horizontal direction is hydrophilic. This tendency is further enhanced by an increase in surface area due to nano-fiberization. Therefore, in the aqueous ink, in a composite material of pigment particles composed of the chitosan nanofibers with an anionic group-containing organic polymer compound described below, the interfacial tension between the pigment particles and the anionic group-containing organic polymer compound is decreased, and repulsive force is imparted to overcome the Van der Waals force between the pigment particles while controlling the charge on the pigment particle surfaces. It is thus considered that a high degree of balance essential for stable dispersion of the pigment can be achieved. When a polysaccharide derivative, particularly carboxymethyl cellulose ammonium as a polysaccharide derivative, is used as the anionic group-containing organic polymer compound, ammonium ion with high bulkiness is considered to contribute to surface potential stabilization of a complex of the pigment particles composed of chitosan nanofibers and the polysaccharide derivative.

The chitosan nanofibers have the tendency of higher hydrophilicity and cationy than cellulose nanofibers and thus have the tendency to exhibit more desired physical properties in a magenta pigment- or yellow pigment-dispersed system with high polarity.

Therefore, even when printing is performed on plain paper containing various paper components, the pigment particles can be fixed without being unnecessarily penetrated into the paper used as an object to be printed, thereby exhibiting a high optical density, causing no color mixing of color inks adjacent to each other in multicolor-type color printing, and causing excellent rubfastness.

In the case of an aqueous ink, particularly, for ink jet, the content of the chitosan nanofibers is preferably in a range of 0.001% to 3%, more preferably 0.01% to 2%, and still more preferably 0.05% to 1% relative to the total ink mass. This is because with the content of less than 0.001%, the optical density and rubfastness cannot be secured, while with the content exceeding 3%, printability is impaired due to an increase in ink viscosity or the like.

The chitosan nanofibers used in the present invention are not particularly limited, and a commercial product and a product produced by a known production method can be used. Chitosan used as a raw material of the chitosan nanofibers is manufactured and sold by many companies of various countries of the world, and it is known that besides commercial products, chitosan with the same structure can be purified from microorganism bacteria or the like. The deacetylation rate of chitosan is not particularly limited and an optimum value may be properly selected according to application. The raw material used is preferably purified chitosan produced by deacetylating chitin possessed by crustaceans such as crabs, shrimps, and the like and then performing protein removal and decalcification. The chitosan nanofibers are produced by fibrillating or refining the chitosan by grinding and/or beating using a refiner, a high-pressure homogenizer, a medium stirring mill, a millstone, a grinder, or the like, and for example, can be produced by a known method such as a method described in Japanese Unexamined Patent Application Publication No. 2011-56456.

The chitosan nanofibers used in the present invention may be a commercial product. Examples of the commercial product include bio-nanofiber “BiNFi-s” chitosan of Sugino Machine Limited. These chitosan nanofibers can be used alone, used as a mixture of two or more types, or used in combination with the cellulose nanofibers.

(Aqueous Medium)

The aqueous pigment dispersion of the present invention uses an aqueous medium such as a water-soluble solvent and/or water as a solvent. In this case, water may be singly used or a mixed solvent of water and a water-soluble solvent may be used. Examples of the water-soluble solvent include ketones such as acetone, methyl ethyl ketone, methyl butyl ketone, methyl isobutyl ketone, and the like; alcohols such as methanol, ethanol, 2-propanol, 2-methyl-1-propanol, 1-butanol, 2-methoxyethanol, and the like; ethers such as tetrahydrofuran, 1,4-dioxane, 1,2-dimethoxyethane, and the like; amides such as dimethylformamide, N-methylpyrrolidone, and the like. A compound selected from the group consisting of ketones having 3 to 6 carbon atoms and alcohols having 1 to 5 carbon atoms is preferably used.

Besides these, a water-soluble organic solvent capable of aqueous dissolution can also be used. Examples thereof include glycols such as ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, propylene glycol, polyethylene glycol, polypropylene glycol, and the like; diols such as butanediol, pentanediol, hexanediol, and similar diols, and the like; glycol esters such as propylene glycol laurate and the like; ethers such as diethylene glycol monoethyl, diethylene glycol monobutyl, diethylene glycol monohexyl, and the like; glycol ethers such as propylene glycol ether, dipropylene glycol ether, cellosolve containing triethylene glycol ether, and the like; alcohols such as methanol, ethanol, isopropyl alcohol, 1-propanol, 2-propanol, 1-butanol, 2-butanol, butyl alcohol, pentyl alcohol, similar alcohols, and the like; sulfolane; lactones such as γ-butyrolactone and the like; lactams such as N-(2-hydroxyethyl)pyrrolidone and the like; other various solvents known as water-soluble organic solvents, such as glycerin and derivatives thereof, polyoxyethylene benzyl alcohol ether, and the like. These water-soluble organic solvents can be used alone or as a mixture of two or more.

In particular, polyhydric alcohols such as glycols and diols with high boiling points, low volatility, and high surface tension are preferred, and glycols such as diethylene glycol, triethylene glycol, and the like are particularly preferred.

(Anionic Group-Containing Organic Polymer Compound)

The anionic group-containing organic polymer compound used in the present invention is an organic polymer compound containing, for example, a carboxyl group, a sulfonic acid group, or a phosphoric acid group. Examples of the anionic group-containing organic polymer compound include polyvinyl resins having anionic groups, polyester resins having anionic groups, amino resins having anionic groups, acrylic resins having anionic groups, epoxy resins having anionic groups, polyurethane resins having anionic groups, polyether resins having anionic groups, polyamide resins having anionic groups, unsaturated polyester resins having anionic groups, phenol resins having anionic groups, silicone resins having anionic groups, fluorine-based polymer compounds having anionic groups, polysaccharide derivatives having anionic groups, and the like.

In particular, acrylic resins having anionic groups and polyurethane resins having anionic groups are preferred from the viewpoint of abundant raw materials, ease of design, and excellent pigment dispersion function.

(Acrylic Resin Having Anionic Group)

Specifically, an acrylic resin having an anionic group is, for example, a resin composed of a copolymer of a monomer having an anionic group, such as (meth)acrylic acid or the like, and another ethylenically unsaturated monomer copolymeriable therewith. In the present invention, “(meth)acrylic acid” represents a general name of acrylic acid and methacrylic acid. Various esters of (meth)acrylic acid are interpreted as the same as described above.

From the viewpoint that hydrophobicity of a copolymer can be enhanced at the same acid value comparison, and adsorption of the copolymer on the pigment surfaces can be further strengthened, preferred examples of the other copolymerizable ethylenically unsaturated monomer include alkyl styrene such as styrene, α-methylstyrene, β-methylstyrene, 2,4-dimethylstyrene, α-ethylstyrene, α-butylstyrene, α-hexylstyrene, and the like; halogenated styrene such as 4-chlorostyrene, 3-chlorostyrene, 3-bromostyrene, and the like; styrene-based monomers such as 3-nitrostyrene, 4-methoxstyrene, vinyltoluene, and the like; and (meth)acrylic acid ester-based monomers having benzene rings, such as benzyl (meth)acrylate, phenyl (meth)acrylate, phenylethyl (meth)acrylate, phenylpropyl (meth)acrylate, phenoxyethyl (meth)acrylate, and the like. In particular, styrene monomers such as styrene, α-methylstyrene, tert-butylstyrene, and the like are preferably used.

The copolymer relating to the acrylic resins having anionic groups in the present invention may be a copolymer containing, as essential polymerization units, a (meth)acrylic acid polymerization unit and another copolymerizable ethylenically unsaturated monomer polymerization unit. The copolymer may be either a bipolymer or a terpolymer or higher-order copolymer with a still another copolymerizable ethylenically unsaturated monomer.

Examples of the ethylenically unsaturated monomer include acrylic acid esters and methacrylic acid esters such as methyl acrylate, methyl methacrylate, n-propyl acrylate, isopropyl acrylate, n-butyl acrylate, sec-butyl acrylate, tert-butyl acrylate, 2-ethylbutyl acrylate, 1,3-dimethylbutyl acrylate, hexyl acrylate, 2-ethylhexyl acrylate, octyl acrylate, ethyl methacrylate, n-butyl methacrylate, 2-methylbutyl methacrylate, pentyl methacrylate, heptyl methacrylate, nonyl methacrylate, and the like; acrylic acid ester derivatives and methacrylic acid ester derivatives such as 3-ethoxypropyl acrylate, 3-ethoxybutyl acrylate, dimethylaminoethyl acrylate, 2-hydroxyethyl acrylate, 2-hydroxybutyl acrylate, ethyl-α-(hydroxymethyl) acrylate, dimethylaminoethyl methacrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, and the like; acrylic acid aryl esters and acrylic acid aralkyl esters such as phenyl acrylate, benzyl acrylate, phenylethyl acrylate, phenylethyl methacrylate, and the like; polyhydric alcohol monoacrylic acid esters and monomethacrylic acid esters such as diethylene glycol, triethylene glycol, polyethylene glycol, glycerin, bisphenol A, and the like; maleic acid dialkyl esters such as dimethyl maleate, diethyl maleate, and the like; vinyl acetate; and the like. These monomers can be added alone or two or more as a monomer component.

The copolymer relating to the acrylic resins having anionic groups in the present invention may be a linear copolymer composed of only a monoethylenically unsaturated monomer polymerization unit or a copolymer having a crosslinked portion and produced by copolymerizing a small amount of any one of various crosslinkable ethylenically unsaturated monomers.

Examples of the crosslinkable ethylenically unsaturated monomers include glycidyl (meth)acrylate, divinylbenzene, and polyhydric alcohol poly(meth)acrylates such as ethylene glycol di(meth)acrylate, propylene glycol di(meth)acrylate, polyethylene glycol di(meth)acrylate, poly(oxyethylene-oxypropylene) glycol di(meth)acrylate, glycerin alkylene oxide-adduct tri(meth)acrylate, and the like.

In the present invention, the reaction rates or the like of the monomers used are considered to be substantially the same, and thus the feeding ratios of the monomers are considered as content ratios by mass of the monomer polymerization units. The copolymer relating to the acrylic resins having anionic groups in the present invention can be synthesized by any one of various known usual reaction methods such as bulk polymerization, solution polymerization, suspension polymerization, emulsion polymerization, and the like. In this case, known common polymerization initiator, chain transfer agent (polymerization degree adjusting agent), surfactant, and defoaming agent can be also used.

Among the copolymers described above as the copolymer relating to the acrylic resins having anionic groups used in the present invention, a styrene-acrylic acid copolymer containing a styrene monomer and (meth)acrylic acid as raw material monomers is particularly preferred, and examples thereof include a styrene-(meth)acrylic acid copolymer, a styrene-(meth)acrylic acid ester-(meth)acrylic acid copolymer, a (meth)acrylic acid ester-(meth)acyclic acid copolymer, and the like. (In the present invention, “styrene-acrylic acid copolymer” is defined as a “copolymer containing a styrene monomer and (meth)acrylic acid as raw material monomers”. Therefore, a general-purpose monomer other than a styrene monomer and (meth)acrylic acid may be copolymerized.)

The styrene-acrylic acid copolymer is produced by copolymerizing a styrene monomer and at least one of an acrylic acid monomer and a methacrylic acid monomer, but both acrylic acid and methacrylic acid are preferably used. The reason for this is that the uniformity of a resin is improved due to improvement in copolymerizability during resin synthesis, resulting in good storage stability and the tendency to produce a pigment dispersion containing finer particles.

During copolymerization, the total amount of a styrene monomer, an acrylic acid monomer, and a methacrylic acid monomer in the styrene-acrylic acid copolymer is preferably 95% by mass or more relative to the whole monomer components.

A usual polymerization method can be used as a method for producing the styrene-acrylic acid copolymer, and examples thereof include methods of performing polymerization reaction in the presence of a polymerization catalyst, such as solution polymerization, suspension polymerization, bulk polymerization, and the like. Examples of the polymerization catalyst include 2,2′-azobis(2,4-dimethylvaleronitrile), 2,2′-azobisisobutyronitrile, 1,1′-azobis(cyclohexane-1-carbonitrile), benzoyl peroxide, dibutyl peroxide, butyl peroxybenzoate, and the like. The amount of use is preferably 0.1 to 10.0% by mass of the monomer components.

The styrene-acrylic acid copolymer may be either a random copolymer or a graft copolymer. The graft copolymer can be exemplified by a graft copolymer in which polystyrene or a copolymer of styrene with a nonionic monomer copolymerizable with styrene serves as a stem or a branch, and a copolymer of acrylic acid, methacrylic acid, and another monomer including styrene serves as a branch or stem. The styrene-acrylic acid copolymer may be a mixture of the graft copolymer and the random copolymer.

In the present invention, the acrylic resins having an anionic group preferably have a weight-average molecular weight within a range of 5,000 to 20,000. For example, when the styrene-acrylic acid copolymer is used, the weight-average molecular weight is preferably within a range of 5,000 to 20,000, and more preferably within a range of 5,000 to 18,000. In particular, the weight-average molecular weight is particularly preferably within a range of 5,500 to 15,000. The weight-average molecular weight is a value measured by GPC (gel permeation chromatography) method and is a value in terms of the molecular weight of polystyrene used as a standard material.

When the anionic group-containing organic polymer compound used in the present invention is the styrene-acrylic acid copolymer, the copolymer has carboxyl groups derived from the acrylic acid monomer and the methacrylic acid monomer and preferably has an acid value of 50 to 220 (mgKOH/g) and more preferably 60 to 200 (mgKOH/g). With the acid value of 220 (mgKOH/g) or less, there is the tendency to produce less aggregation of the pigment.

The acid value is a value measured according to Japanese Industrial Standards “K0070:1992, Test methods for acid value, saponification value, ester value, iodine value hydroxyl value, and unsaponifiable matter of chemical products” and represents an amount (mg) of potassium hydroxide necessary for completely neutralizing 1 g of resin.

With the excessively low acid value, pigment dispersion and storage stability are decreased, and when an aqueous pigment dispersion for ink jet recording described below is prepared, printing stability is undesirably degraded. With the excessively high acid value, the water resistance of a color recorded image is undesirably degraded. In order to bring the acid value of the copolymer within the range, copolymerization may be performed by using (meth)acrylic acid so that the acid value falls within the range.

(Polyurethane Resin Having Anionic Group)

Examples of the polyurethane resins having anionic groups used in the present invention include polyols and polyisocyanates each having an anionic group such as a carboxyl group, a sulfonic acid group, or the like, and urethane resins produced by further reacting general-purpose polyol not having an anionic group and a chain extender according to demand.

Example of the polyol having a carboxyl group used in the present invention include esters produced by reacting polyhydric alcohols with polybasic acid anhydrides, dihydroxyalkanoic acids such as 2,2-dimethylol lactic acid, 2,2-dimethylol propionic acid, 2,2-dimethylol butanoic acid, 2,2-dimethylol valeric acid, and the like. Preferred compounds include 2,2-dimethlylol propionic acid and 2,2-dimethylol butanoic acid. In particular, dimethylol propionic acid or dimethylol butanoic acid is preferred because of its easy availability. Example of the polyol having a sulfonic acid group include polyester polyols produced by reacting a dicarboxylic acid such as 5-sulfoisophthalic acid, sulfoterephthalic acid, 4-sulfophthalic acid, 5[4-sulfophenoxy]isophthalic acid, or the like, a salt thereof, and the low-molecular-weight polyol described above.

Examples of the diisocyanate used in the present invention include aliphatic diisocyanate compounds such as hexamethylene diisocyanate, 2,2,4-trimethylhexamethylene diisocyanate, and the like; alicyclic diisocyanate compounds such as isophorone diisocyanate, hydrogenated xylylene diisocyanate, 4,4-cyclohexylmethane diisocyanate, and the like; araliphatic diisocyanate compounds such as xylylene diisocyanate, tetramethylxylene diisocyanate, and the like; aromatic diisocyanate compounds such as toluylene diisocyanate, phenylmethane diisocyanate, and the like.

Among these, aliphatic diisocyanate compounds or alicyclic diisocyanates are preferred from the viewpoint of little photodiscoloration of a printed image.

Examples of the general-purpose polyol not having an anionic group include polyester polyol, polyether polyol, polyhydroxy polycarbonate, polyhydroxy plolyacetal, polyhydroxy polyacrylate, polyhydroxy polyesteramide, polyhydroxy polythioether, and the like. Among these, polyester polyol, polyether polyol, and polyhydroxy polycarbonate are preferred. The polyols may be reacted alone or as a mixture of two or more.

Besides the polyol, a low-molecular-weight diol may be properly combined for the purpose of adjusting the film hardness or the like of a print matter. Examples of the diol include ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, 1,2-propanediol, 1,3-propanediol, 1,4-butanediol, and the like.

Examples of the chain extender used in the present invention include diols such as ethylene glycol, propylene glycol, 1,4-butanediol, 1,6-hexanediol, 1,9-nonanediol, 1,4-bis(β-hydroxyethoxy)benzene, 1,4-cyclohexanediol, xylylene glycol, and the like; diamines such as ethylenediamine, propylenediamine, xylylenediamine, isophoronediamine, 4,4′-diaminodiphenylmethane, tolylenediamine, 4,4′-diaminodicyclohexylmethane, and the like. These can be used alone or combination of two or more.

The polyurethane resin can be produced by producing a urethane resin by reacting the polyol and the polyisocyanate without a solvent or in the presence of an organic solvent. Next, the urethane resin having an anionic group formed by neutralization with the basic compound or the like is made aqueous by mixing in an aqueous medium. During the mixing, if required, the chain extender is mixed and reacted.

The reaction of the polyol with the polyisocyanate is performed, for example, under a condition in which the equivalent ratio of isocyanate groups possessed by the polyisocyanate to hydroxyl groups possessed by the polyol is preferably within a range of 0.8 to 2.5 and more preferably within a range of 0.9 to 1.5.

The weight-average molecular weight of the polyurethane resin having an anionic group used in the present invention is preferably within a range of 5,000 to 500,000, more preferably 10,000 to 200,000, and particularly preferably 15,000 to 100,000.

The weight-average molecular weight is a value measured by GPC (gel permeation chromatography) method and is a value in terms of the molecular weight of polystyrene used as a standard material.

Also, the polyurethane resin used preferably has an acid value within a range of 2 to 200 (mgKOH/g) and preferably within a range of 2 to 100 (mgKOH/g) for improving good water dispersion stability or the like of the polyurethane resin.

The acid value is a value measured according to Japanese Industrial Standards “K0070:1992, Test methods for acid value, saponification value, ester value, iodine value hydroxyl value, and unsaponifiable matter of chemical products” and represents an amount (mg) of potassium hydroxide necessary for completely neutralizing 1 g of resin.

With the excessively low acid value, pigment dispersion and storage stability may be decreased, while with the excessively high acid value, the water resistance of a formed image may be degraded. In order to bring the acid value of the copolymer within the range, copolymerization may be performed by using the polyol having a carboxyl group so that the acid value falls within the range.

(Neutralizing Agent for Acryl Resin Having Anionic Group and Polyurethane Resin Having Anionic Group)

In the present invention, the acryl resin having an anionic group and the polyurethane resin having an anionic group are preferably used after neutralized with a basic compound. A known compound can be used as the basic compound, and examples thereof include hydroxides of alkali metals such as potassium, sodium, and the like; carbonates of alkali metals such as potassium, sodium, and the like; carbonates of alkaline-earth metals such as calcium, barium, and the like; inorganic basic compounds such as ammonium hydroxide and the like; organic basic compounds such as aminoalcohols, such as triethanolamine, N,N-dimethanolamine, N-aminoethylethanolamine, dimethylethanolamine, N—N-butyldiethanolamine, and the like; morpholines, such as morpholine, N-methylmorpholine, N-ethylmorpholine, and the like; piperazine such as N-(2-hydroxyethyl)piperazine, piperazine hexahydrate, and the like. Among these, alkali metal hydroxides represented by potassium hydroxide, sodium hydroxide, and lithium hydroxide are preferred in view of contribution to a decrease in viscosity of the aqueous pigment dispersion and discharge stability of an ink for aqueous ink jet recording, and potassium hydroxide is particularly preferred.

The neutralization rate of the anionic group with the basic compound is not particularly limited but is generally frequently within a range of 80% to 120%. In the present invention, the neutralization rate is a value indicating an amount by % of the basic compound added relative to the amount necessary for neutralizing all carboxyl groups in the anionic group-containing organic polymer compound and is calculated by a formula below.

Neutralization rate (%)=[{mass (g) of basic compound×56.11×1000}/{resin acid value (mgKOH/g)×equivalent of basic compound×resin amount (g)}]×100  [Math. 3]

(Polysaccharide Derivative Having Anionic Group)

In the present invention, also, a polysaccharide derivative having an anionic group is preferably mixed with the aqueous pigment dispersion. The polysaccharide derivative having an anionic group is not particularly limited as long as it is a polyanionic polysaccharide. Examples thereof include natural polysaccharides such as hyaluronic acid, alginic acid, pectin, polygalacturonic acid, and the like; carboxyalkyl polysaccharides such as carboxymethylpullulan, carboxymethylchitin, carboxymethylchitosan, carboxymethylmannan, carboxymethyl starch, carboxymethyl dextran, carboxyethyl cellulose, carboxymethyl pullulan, and the like; oxidized polysaccharides such as oxidized cellulose, oxidized starch, and the like; and polysaccharides containing sulfuric acid groups such as chondroitin sulfate, dermatan sulfate, heparin and heparin sulfate, and the like. Among these, carboxymethyl cellulose and hyaluronic acid are preferred, and carboxymethyl cellulose is particularly preferred. The weight-average molecular weight of the polysaccharide as a raw material is not particularly limited but may be selected according to purpose because the viscosity tends to increase as the polymerization degree increases. It suffices to say that for example, the weight-average molecular weight is preferably 50,000 or more and 1,000,000 or less and more preferably 50,000 or more and 500,000 or less.

In the present invention, the polysaccharide derivative having an anionic group preferably forms a salt with cation. Examples of the cation which forms a salt with the polysaccharide derivative having an anionic group include, but are not particularly limited to, proton, and metal ions, specifically metal ions of sodium, potassium, lithium, calcium, magnesium, and the like; and organic cations such as organic ammonium and the like. Among these, carboxymethyl cellulose sodium salt and carboxymethyl cellulose ammonium salt are preferred because they can be easily obtained and the intended purpose can be easily obtained, and the carboxymethyl cellulose ammonium salt is particularly preferred because of the large viscosity decreasing effect. Of course, these polysaccharide derivatives having anionic groups can be used alone or in combination of two or more.

The degree of etherification (also referred to as a “degree of substitution” DS) and the degree of neutralization of the polysaccharide derivative having an anionic group, particularly carboxymethyl cellulose sodium salt or ammonium salt, used in the present invention are not particularly limited but are preferably adjusted so that the viscosity of a 1 mass % aqueous solution measured by a B-type viscometer at a rotor rotational speed of 60 rpm and 25° C. is 300 to 7000 mPa·s and more preferably 500 to 5000 mPa·s. With the viscosity exceeding 7000 mPa·s, uniform pigment dispersion tends to become difficult, and the viscosity of the resultant ink is excessively increased, thereby causing practical disadvantage. On the other hand, with the viscosity of less than 300 mPa·s, significant improvement in adhesion and rubfastness to a medium tends to be hardly recognized, thereby causing disadvantage.

The “degree of etherification” is a value indicating an average number of hydroxyl groups, to which carboxymethyl groups are ether-bonded, among the three hydroxyl groups contained in anhydrous glucose serving as a cellulose constitution unit in carboxymethyl cellulose. Therefore, the value is theoretically between 0 and 3.

The degree of etherification of carboxymethyl cellulose sodium salt or ammonium salt used in the present invention is preferably 0.5 to 2, more preferably 0.6 to 1.6, and still more preferably 0.8 to 1.4. This is because the degree of etherification of 0.8 or more causes salt resistance. The upper limit of the degree of etherification is theoretically 3, and the degree of etherification exceeding 2 causes difficulty in stable production, while the degree of etherification of less than 0.4 causes difficulty in dissolving in an aqueous medium and thus causes low practicality.

The degree of etherification can be determined, for example, according to a CMC Industry Association analytical method (ashing method). First, 1 g of carboxymethyl cellulose is weighed, placed in a magnetic crucible, and ashed at 600° C., and the sodium oxide produced by ashing is titrated with 0.05 mol/L sulfuric acid using phenolphthalein as an indicator. The degree of etherification can be determined by calculation according to a formula below in which a titer A (mL) per g of carboxymethyl cellulose is introduced.

Degree of etherification=(162×A)/(10,000−80×A)  [Math. 4]

For a commercial product, a value described in a catalogue can be directly used.

The amount of the polysaccharide derivative having an anionic group mixed is not particularly limited and appropriately determined according to the purpose described above. For example, for the purpose of improving the color development (optical density) of the formed image and the rubfastness of the image, the amount of the polysaccharide derivative having an anionic group is preferably 5 parts by mass or less, more preferably 3 parts by mass or less, and most preferably 2 parts by mass or less relative to 1 part by mass of cellulose crystal.

The carboxymethyl cellulose sodium or carboxylmethyl cellulose ammonium used may be a commercial product. Examples thereof include Serogen series sold by DKS Co., Ltd., CMC Daicel series sold by Daicel FineChem Ltd., Sunrose F series sold by Nippon Paper Chemicals Co., Ltd., and the like. Also, DN series sold by Daicel FineChem Ltd. can be used as the carboxymethyl cellulose ammonium.

In the case of the aqueous pigment dispersion, particularly for ink jet, the content (mass basis) of the anionic group-containing organic polymer compound used in the present invention is preferably within a range of 0.1% to 10%, more preferably 0.3% to 5%, and still more preferably 0.5% to 2% relative to the total mass of ink. This is because with the content of less than 0.1%, rubfastness cannot be secured, while with the content exceeding 10%, printability is degraded due to an increase in viscosity or the like.

The anionic group-containing organic polymer compound is mainly used for the purpose of dispersing the pigment, but the compound has the function as a binder because it is a polymer.

Of course, a commercial product can also be used. Examples of the commercial product include Ajisper PB series of Ajinomoto Fine-Techno Co., Inc., DISPERBYK series and BYK series of BYK Co., Ltd., Efka series of BASF Corporation, and the like.

(Method for Producing Aqueous Pigment Dispersion)

A method for producing the aqueous pigment dispersion of the present invention is not particularly limited, and a known method can be used. That is, bio-nanofibers or the like can be mixed with desired timing regardless of before or after medialess dispersion described below. Examples of the method include (1) a method for preparing an aqueous pigment dispersion containing at least the pigment, the bio-nanofibers, etc. of the present invention and, if required, other additives added thereto, by medialess dispersion, (2) a method for preparing an aqueous pigment dispersion by forming a high-concentration pigment aqueous dispersion (pigment paste) in advance, and then diluting the prepared aqueous dispersion with an aqueous medium and, at the same time, adding the bio-nanofibers and, if required, other additives, and the like.

(1) Medialess Dispersion of Aqueous Pigment Dispersion

In the present invention, examples of the medialess dispersion include an ultrasonic dispersion method, and dispersion methods using a high-speed disc impeller, a colloid mill, a roll mill, a high-pressure homogenizer, a nanomizer, an altimizer, or the like. In view of productivity and contamination (mixing and contamination with foreign matter) due to wearing of a medium, the ultrasonic dispersion method is preferred. In the present invention, an example using the ultrasonic dispersion method is described in detail below.

It is preferred to mix and stirrer the pigment and the aqueous medium before ultrasonic dispersion in order to enhance flowability or prevent settling of the pigment, but this is not essential and a mixing-stirring apparatus is not particularly limited.

Also, from the viewpoint of securing flowability, the viscosity is preferably within a range of 0.1 to 100 mPa·s, more preferably 0.5 to 50 mPa·s, still more preferably 0.5 to 30 mPa·s, and most preferably 1.0 to 20 mPa·s. In this case, the pigment concentration is preferably 1% to 30% by mass, more preferably 1% to 25% by mass, still more preferably 3% to 20% by mass, and most preferably 5% to 20% by mass.

Ultrasonic irradiation conditions are not particularly limited, but the irradiation can be preferably performed at an output of 100 to 3000 W and a frequency of 15 to 40 kHz and more preferably at an output of 150 to 2000 W and a frequency of 15 to 30 kHz.

At the output and frequency within the respective ranges described above, a dispersion step by cavitation can be effectively performed, and the number of coarse particles in the aqueous pigment dispersion is decreased, thereby improving chroma (texture) of a color film obtained from the aqueous pigment dispersion and permitting smooth discharge (good discharge stability) in ink jet printing with aqueous ink using the aqueous pigment dispersion. Further, the output and frequency are very preferred for the reasons that the quality of a product is not decreased by settling of the pigment particles or the like, that erosion of an oscillating rod is significantly decreased to decrease the maintenance cost of the device used, and the like.

A time necessary and sufficient for actually uniformly dispersing pigment particles, bio-nanofibers, etc. in the aqueous pigment dispersion may be secured as the time of ultrasonic irradiation. An amount of electric power of 5 to 100 W/g is generally applied to the mass of the pigment contained in the dispersion. Of course, ultrasonic treatment may be performed for a longer time or stopped in a short time. The ultrasonic treatment time is preferably selected within a range in which no trouble occurs in performance such as the dispersed particle diameter, viscosity, image clearness, and the like according to the type of the pigment, and consideration is made to prevent a decrease in productivity with time.

After the ultrasonic irradiation, if required, the aqueous pigment dispersion can be further dispersed. Also, dispersion and ultrasonic irradiation can be repeatedly performed.

Any one of various known system devices can be used as a dispersing device which can be used in the dispersion step, and the dispersing device is not particularly limited. Examples of the device include media dispersion devices such as a sand mill, a beads mill, a pebble mill, a ball mill, a pearl mill, a basket mill, an attritor, a Dyno-mill, a bore mill, a visco-mill, a motor mill, a SC mill, a dry mill, a paint conditioner, and the like; and medialess dispersing devices such as a high-speed disc impeller, a colloid mill, a high-pressure homogenizer, a nanomizer, an altimizer, and the like. However, it should be noted that as described above, unnecessary physical damage may be caused on the pigment surfaces.

The temperature of the aqueous pigment dispersion subjected to ultrasonic irradiation is not particularly limited but the ultrasonic irradiation is preferably performed while the aqueous pigment dispersion is controlled to the freezing point to 70° C. This is because at a temperature equal to or lower than the freezing point, ultrasonic dispersion becomes impossible, while at a temperature 70° C. or higher, an uncertain condition such as an increase in pigment concentration occurs due to water evaporation or the like.

A known method of ice cooling, air cooling, water cooling, or the like can be generally used as a method for cooling the aqueous pigment dispersion during ultrasonic irradiation. Examples of the method include a method of flowing a refrigerant in a jacket of a vessel in which the aqueous pigment dispersion is placed, a method of immersing a vessel containing the aqueous pigment dispersion in a refrigerant, a method of spraying gas wind, a method of cooling by evaporation heat using a refrigerant, such as water, and wind, and the like.

For example, a method using, as a refrigerant, cooling water previously cooled to over 0° C. and 20° C. or lower and preferably over 0° C. and 10° C. or lower is a desired method because it is relatively economical and has an excellent cooling efficiency. In this case, the cooling water can be circulated by a circulating device, and at the same time, cooling can be performed with a cooling device. In this case, it is very preferred to cause freezing-point depression by adding, to the cooling water, ethylene glycol, diethylene glycol, or the like which decreases the freezing temperature, or adding sodium chloride or the like. As a result, even when a satisfactory cooling effect cannot be obtained by cooling water of over 0° C., the cooling water at a temperature lower than this can be produced, and thus ultrasonic irradiation can be performed while the aqueous pigment dispersion is maintained at a lower temperature with the temperature range described above. Even in the case of air cooling, instead of simply spraying wind at an ambient temperature, cold air previously cooled is preferably used.

In relation to cost, the ultrasonic irradiation is preferably performed by using as few devices as possible but, if required, a minimum number of devices can be connected in series or parallel for treatment.

The end point of ultrasonic irradiation may be determined by measuring the particle diameters of the pigment particles and the composite particles using a particle gauge or a commercial particle diameter measuring device, or by measuring physical properties such as viscosity, contact angle, reflected luminous intensity and hue of coating films prepared by various methods, etc. Also, the end point may be determined by direct observation with a microscope or the like.

(2) Method Passing Through High-Concentration Aqueous Pigment Dispersion (Pigment Paste)

A method for previously forming the pigment paste is not particularly limited, and a known dispersion method can be used.

Examples of the method for preparing the pigment paste include methods (i) to (iii) below.

(i) A method of adding a pigment to an aqueous medium containing a pigment dispersant and water and then dispersing the pigment in the aqueous medium by using a stirring/dispersion device to prepare a pigment paste.

(ii) A method of kneading a pigment and a pigment dispersant by using a kneader such as a two-roll, a mixer, or the like, and then adding the resultant kneaded product to an aqueous medium containing water to prepare a pigment paste by using a stirring/dispersion device.

(iii) A method of adding a pigment to a solution prepared by dissolving a pigment dispersant in an organic solvent having compatibility with water, such as methyl ethyl ketone, tetrahydrofuran, or the like, dispersing the pigment in the organic solution by using a stirring/dispersion device, next performing phase-inversion emulsification using an aqueous medium, and then distilling off the organic solvent to prepare a pigment paste.

Examples of the kneader include, but are not particularly limited to, a Henschel Mixer, a pressure kneader, a Banbury mixer, a planetary mixer, and the like.

Examples of the stirring/dispersion device include, but are not particularly limited to, an ultrasonic homogenizer, a high-pressure homogenizer, a paint shaker, a ball mill, a roll mill, a sand mill, a sand grinder, a Dyno-mill, Dispermat, a SC mill, a nanomizer, and the like. These devices may be used alone or in combination of two or more.

The amount of the pigment contained in the pigment paste is preferably 5% to 60% by mass and more preferably 10% to 50% by mass. When the amount of the pigment is less than 5% by mass, there is a tendency that coloring of the aqueous pigment dispersion and aqueous ink prepared by using the pigment paste is unsatisfactory, and a satisfactory image density cannot be obtained. Conversely, when the amount exceeds 60% by mass, the dispersion stability of the pigment in the pigment paste tends to be decreased.

Also, remaining coarse particles cause deterioration in various image characteristic, and thus the coarse particles are preferably properly removed by centrifugal separation or filtration treatment or the like after preparation of an ink.

After the dispersion step, post-treatment may be performed through a step of removing impurities by ion exchange treatment or ultra-treatment. Ionic substances (divalent metal ions and the like) such as cation and anion can be removed by ion exchange treatment, and impurity dissolved materials (residual materials of pigment synthesis, excessive components in the dispersion composition, resins not adsorbed on the organic pigment, mixed foreign matters, etc.) can be removed by ultra-treatment. The ion exchange treatment uses a known ion-exchange resin. The ultra-treatment uses a known ultrafiltration membrane which may be a usual type or two-times capacity-up type.

(Aqueous Ink for Ink Jet Recording)

If required, the aqueous pigment dispersion can be diluted with a water-soluble solvent with any desired timing, or a wetting agent (drying inhibitor), a penetrant, or another additive, that is, a known common additive, can be added. The addition permits use for various applications such as the automobile or construction coating field, the printing ink field of offset inks, gravure inks, flexo inks, silk screen inks, and the like, the field of inks for ink jet printing, and the like. After preparation of an ink, a centrifugal separation or ultrafiltration treatment step can be added for removing coarse particles. Herein, an aqueous ink for ink jet recording is described in detail.

(Wetting Agent)

The wetting agent is added for the purpose of preventing drying of the ink. The content of the wetting agent for the purpose of preventing drying in the ink is preferably 3% to 50% by mass.

The wetting agent used in the present invention is not particularly limited and preferably has miscibility with water and the effect of preventing clogging of a head of an ink jet printer. Examples thereof include glycerin, ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol having a molecular weight of 2000 or less, propylene glycol, dipropylene glycol, tripropylene glycol, 1,3-propylene glycol, isopropylene glycol, isobutylene glycol, 1,4-butanediol, 1,3-butanediol, 1,5-pentanediol, 1,6-hexanediol, mesoerythritol, pentaerythritol, and the like. In particular, when propylene glycol or 1,3-butyl glycol is contained, safety and the excellent effect on ion drying properties and discharge performance can be achieved.

(Penetrant)

The penetrant is added for the purpose of improving the penetration into a recording medium and adjusting the dot diameter on a recording medium.

Examples of the penetrant include lower alcohols such as ethanol, isopropyl alcohol, and the like, alkyl alcohol ethylene oxide adducts such as ethylene glycol hexyl ether, diethylene glycol butyl ether, and the like, alkyl alcohol propylene oxide adducts such as propylene glycol propyl ether and the like.

The content of the penetrant in the ink is preferably 0.01% to 10% by mass.

(Surfactant)

The surfactant is added for adjusting ink characteristics such as surface tension and the like. Examples of the surfactant which can be added include, but are not particularly limited to, various anionic surfactants, nonionic surfactants, cationic surfactants, and amphoteric surfactants, and the like. Among these, the anionic surfactants and the nonionic surfactants are preferred.

Examples of the anionic surfactants include alkylbenzenesulfonic acid salts, alkylphenylsulfonic acid salts, alkylnaphthalenesulfonic acid salts, higher fatty acid salts, sulfuric acid ester salts of higher fatty acid esters, sulfonic acid salts of higher fatty acid esters, sulfuric acid ester salts and sulfonic acid salts of higher alcohol ethers, higher alkyl sulfosuccinic acid salts, polyoxyethylene alkyl ether carboxylic acid salts, polyoxyethylene alkyl ether sulfuric acid salts, alkylphosphoric acid salts, polyoxyethylene alkyl ether phosphoric acid salts, and the like. Specific examples thereof include dodecylbenzenesulfonic acid salts, isopropylnaphthalenesulfonic acid salts, monobutylphenylphenol monosulfonic acid salts, monobutylbiphenylsulfonic acid salts, dibutylphenylphenol disulfonic acid salts, and the like.

Examples of the nonionic surfactants include polyoxyethylene alkyl ethers, polyoxyethylene alkyl phenyl ethers, polyoxyethylene fatty acid esters, sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol fatty acid esters, glycerin fatty acid esters, polyoxyethylene glycerin fatty acid esters, polyglycerin fatty acid esters, sucrose fatty acid esters, polyoxyethylene alkylamines, polyoxyethylene fatty acid amides, fatty acid alkylolamides, alkylalkanol amides, acetylene glycol, acetylene glycol oxyethylene adduct, polyethylene glycol-polypropylene glycol block copolymers, and the like. Among these, preferred are polyoxyethylene nonyl phenyl ether, polyoxyethylene octyl phenyl ether, polyoxyethylene dodecyl phenyl ether, polyoxyethylene alkyl ethers, polyoxyethylene fatty acid esters, sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, fatty acid alkylolamides, acetylene glycol, acetylene glycol oxyethylene adduct, and polyethylene glycol-propylene glycol block copolymers.

Other examples of the surfactant which can be used include silicone-based surfactants such as polysiloxane oxyethylene adduct; fluorine-based surfactants such as perfluoroalkylcarboxylic acid salts, perfluoroalkylsulfonic acid salts, and oxyethylene perfluoroalkyl ethers; bio-surfactants such as spiculisporic acid, rhamnolipid, and lysolecithin, and the like.

These surfactants can be used alone or as a mixture of two or more. When the surfactant is added, the adding amount is preferably within a range of 0.001% to 2% by mass, more preferably within a range of 0.001% to 1.5% by mass, and still more preferably within a range of 0.01% to 1% by mass relative to the total mass of ink. When the amount of the surfactant added is less than 0.001% by mass, there is a tendency that the effect of addition of the surfactant cannot be obtained, while when the amount of use exceeds 2% by mass, the problem of image blurring or the like easily occurs.

If required, an antiseptic agent, a viscosity adjuster, a pH adjuster, a chelating agent, a plasticizer, an antioxidant, an ultraviolet absorber, and the like can also be added.

(Recording Media)

The aqueous pigment dispersion of the present invention exhibits a high optical density and rubfastness, particularly, for plain paper. Of course, the aqueous pigment dispersion may be used for other absorbent recording media. Examples of a water absorbent recording medium include plain paper, (fine) coated paper, cloth, paper for exclusive use for ink jet, ink jet glossy paper, corrugated cardboard, wood, and the like.

EXAMPLES

The present invention is described in detail by giving examples below.

In addition, “parts” and “%” are “parts by mass” and “% by mass”, respectively, unless otherwise specified.

<Bio-Nanofibers>

The bio-nanofibers shown in Table 1 were used.

TABLE 1 Bio-nanofiber Cellulose nanofiber Cellulose nanofiber Chitosan nanofiber Product name Celish BiNFi-s BiNFi-s KY100G 2% cellulose chitosan Maker Daicel FineChem Sugino Machine Sugino Machine Ltd. Limited Limited Product name CEL-KY CEL-NF CHI-NF (abbreviation) Aspect ratio 160 270 430 Mode diameter 340 nm 410 nm 320 nm 80% particle diameter/  5.7  5.3  5.3 20% particle diameter Specific surface area — 2059 cm²/cm³ 1959 cm²/cm³ Degree of 58% — — crystallization Amount of carboxyl Less than 0.1 mmol/g Less than 0.1 mmol/g — group

The average fiber diameter and aspect ratio are calculated from the results of SEM analysis. Specifically, a bio-nanofiber dispersion was cast on a wafer and observed with SEM, and fiber diameter and fiber length values of 20 or more fibers per image are read. This was performed for images of at least three regions which were not overlapped with each other, to obtain information of the fiber diameters and fiber lengths of at least 30 fibers. The average fiber diameter was calculated to two significant figures from the date of fiber diameters. The average fiber length was calculated from the date of fiber lengths, and the aspect ratio was calculated to two significant figures by aspect ratio=average fiber diameter/average fiber length.

The mode diameter and (80% particle diameter/20% particle diameter) were calculated to two significant figures from measurement values (volume basis) of 0.1% by mass of bio-nanofibers (solvent:water, temperature 25° C.) by using dynamic light scattering Nanotrac particle size analyzer UPA-150EX (manufactured by Nikkiso Co., Ltd.).

The specific surface area was calculated from particle size distribution values measured by a light scattering method using laser diffraction/scattering particle size distribution analyzer LA-960 (manufactured by Horiba, Ltd.). The measurement conditions are given below.

Measurement range: 0.01 μm to 3,000 μm, measurement method: wet method, basis of the particle diameter: volume, dispersion medium: pure water

Sample refractive index: 1.56 to 0.00i, dispersion medium refractive index: 1.333 to 0.00i

Dispersion treatment: built-in ultrasonic waves (30 W) 1 minute, circulation speed: 3, stirring speed: No

Transmittance (semiconductor laser beam) and transmittance (LED light): 80% or more

The degree of crystallization of cellulose was calculated according to a formula below from the diffraction intensity of a 002 plane at 2θ=22.6° and the diffraction intensity of an amorphous portion at 2θ=18.5° using the diffraction intensity at 2θ=4° to 32° as a baseline in a diffraction chart obtained by measurement of X-ray crystal diffraction (apparatus: RINT-2000 (manufactured by Rigaku Corporation)) at a measurement voltage of 40 kV, a measurement current of 50 mA, and a scan speed of 2°/min.

χ_(c)=(I _(002c) −I _(a))/I _(002c)×100  [Math. 5]

(In the formula, χ_(c) represents the degree of crystallization of type I cellulose (%), I_(002c) represents the 002 plane diffraction intensity at 2θ=22.6°, and I_(a) represents the amorphous portion diffraction intensity at 2θ=18.5°.)

<Anionic Group-Containing Organic Polymer Compound>

The following compounds were used as the anionic group-containing organic polymer compound.

(Polysaccharide Derivative Having Anionic Group)

Commercial products were used.

CMC139O (manufactured by Daicel FineChem Ltd.): sodium carboxylmethyl cellulose (etherification degree, 1.0 to 1.5)

DN-800H (manufactured by Daicel FineChem Ltd.): ammonium carboxylmethyl cellulose

DN-100L (manufactured by Daicel FineChem Ltd.): ammonium carboxylmethyl cellulose

DN-10L (manufactured by Daicel FineChem Ltd.): ammonium carboxylmethyl cellulose

Acrylic Resin Having Anionic Group Production Example 101 Solution (SA-1) of Acrylic Resin Having Anionic Group

A resin A having a monomer composition ratio (styrene/methacrylic acid/acrylic acid) of 77/13/10 (mass ratio), a weight-average molecular weight of 8800, an acid value of 150 mgKOH/g, and a glass transition temperature of 107° C. was produced. Then, 87.4 parts of ion exchange water and 22 g of a 34 mass % aqueous potassium hydroxide (KOH) solution were added to 50 parts of methyl ethyl ketone (abbreviated as “MEK” hereinafter) and 50 parts of the resin A, and the resultant mixture was sufficiently stirred to prepare a resin solution. Then, MEK was removed from the resin solution at a water bath temperature of 45° C. under a reduced pressure condition of 40 hPa, thereby preparing a solution (SA-1) of an acrylic resin having an anionic group with a resin sold content of 20%.

Polyurethane Resin Having Anionic Group Production Example 102 Solution (UR-1) of Polyurethane Resin Having Anionic Group

In a vessel replaced with nitrogen and provided with a thermometer, a nitrogen gas inlet tube, and a stirrer, 64.2 parts by mass of methyl ethyl ketone was added, and 18.4 parts by mass of 2,2-dimethylol propionic acid and 33.9 parts by mass of isophorone diisocyanate were mixed in the methyl ethyl ketone, followed by reaction at 80° C. for 4 hours. Four hours after, 38.2 parts by mass of methyl ethyl ketone was further supplied and the resultant mixture was cooled to 60° C. or lower, and 140.1 parts by mass of polyether polyol (“PTMG2000” polytetramethylene glycol manufactured by Mitsubishi Chemical Corporation, number-average molecular weight 1,000) and 0.01 parts by mass of dibutyltin dilaurate (hereinafter “DBTDL”) were added and continuously reacted at 80° C.

After it was confirmed that the weight-average molecular weight of the reaction product reached a range of 20,000 to 50,000, the reaction is terminated by adding 1.3 parts by mass of methanol. Next, 41.6 parts by mass of methyl ethyl ketone was added to the reaction product to prepare an organic solvent solution of urethane resin.

The carboxyl groups possessed by the urethane resin were partially or entirely neutralized by adding 15.1 parts by mass of a 50 mass % aqueous potassium hydroxide solution to the urethane resin organic solvent solution. Next, 848.5 parts by mass of water was added and sufficiently stirred to produce a mixture containing the urethane resin, methyl ethyl ketone, and water, the urethane resin being dispersed or dissolved in the water.

Next, after aging of the mixture for about 2 hours, 0.07 parts by mass of Surfynol 440 (manufactured by Air Products and Chemicals, Inc., acetylene glycol ethylene oxide adduct, nonvolatile content 100% by mass) was added to the mixture and stirred for about 20 minutes to produce a mixture, which was then distilled under a reduced pressure condition of about 1 to 50 kPa.

After it was confirmed that 144 parts by mass of methyl ethyl ketone contained in the mixture was removed, 0.03 parts by mass of Surfynol 440 (manufactured by Air Products and Chemicals, Inc.,) was added under reduced pressure, and then distillation under reduced pressure was continued. Next, after it was confirmed that 147 parts by mass of water contained in the mixture was removed, the reduced-pressure distillation was terminated.

Next, the nonvolatile content was adjusted by adding water to prepare a solution (UR-1) of a polyurethane resin having an anionic group with a resin sold content of 20% by mass.

<Pigment or the Like>

Commercial products below were used as the pigment or the like.

(Pigment)

#960 (manufactured by Mitsubishi Chemical Corporation): carbon black

FASTOGEN Blue TGR (manufactured by DIC Corporation): C.

I. Pigment Blue 15:3

FASTOGEN Super Magenta RY (manufactured by DIC Corporation): C. I. Pigment Red 122

Fast Yellow 7413 (manufactured by Sanyo Color Works, Ltd.): C. I. Pigment Yellow 74

(Self-Dispersion Type Pigment Dispersion)

Pigment dispersions below were used as a self-dispersion type pigment dispersion.

CAB-O-JET 400 Black Colorant (United States Cabot Corporation)

CAB-O-JET 450C Cyan Colorant (United States Cabot Corporation)

CAB-O-JET 465M Magenta Colorant (United States Cabot Corporation)

CAB-O-JET 470Y Yellow Colorant (United States Cabot Corporation)

SENSIJET BLACK SDP100 (manufactured by United States Sensient Colors Inc.)

Production Example 1 Method for Producing Ultrasonic Dispersion (US) Aqueous Black Pigment Dispersion

In a metal beaker, 20 parts of “#960” (carbon black manufactured by Mitsubishi Chemical Corporation), 20 parts of the solution (SA-1) of the anionic group-containing organic polymer compound, 5 parts of triethylene glycol, and water were added so that a total amount was 100 parts, and the resultant mixture was manually stirred. Then, ultrasonic dispersion was performed with an ultrasonic disperser (UP200St manufactured by Hielscher Company, operation frequency: 26 KHz, operation output: 160 W) for 10 minutes. After the ultrasonic dispersion treatment, 1.0 part (in terms of solid content) of bio-nanofibers “BiNFi-s 2% cellulose” (manufactured by Sugino Machine Limited, product name (abbreviation): CEL-NF), and pure water were added to 100 parts of the mixture so that a total amount was 250 parts, followed by manual stirring. Then, ultrasonic dispersion treatment was performed with an ultrasonic disperser (UP200St manufactured by Hielscher Company, operation frequency: 26 KHz, operation output: 160 W) for 25 minutes to produce an aqueous black pigment dispersion (corresponding to a pigment concentration of 8%).

Production Examples 2 to 4 Method for Producing Ultrasonic Dispersion (US) Aqueous Cyan Pigment Dispersion

An aqueous cyan pigment dispersion was prepared by the same method as described above except that the type of the pigment used, the type of the anionic group-containing organic polymer compound used, and the type and amount of the bio-nanofibers used were changed to those described in each of examples.

Table 2 shows examples of the amount of ultrasonic dispersion (US) aqueous pigment dispersion added. When a self-dispersion type pigment was used as the pigment, bio-nanofibers or the like were added to a dispersion of the self-dispersion type pigment so as to prepare a predetermined composition.

TABLE 2 Production of ultrasonic dispersion (US) aqueous pigment dispersion Production Production Production Production Example 1 Example 2 Example 3 Example 4 (Black) (Cyan) (Magenta) (Yellow) Pigment Product name #960 FASTOGEN FASTOGEN Fast Yellow Blue TGR Super Magenta 7413 RY (parts) 20 20 20 20 Solution of anionic group-containing 20 30 30 20 Organic polymer compound (SA-1) (parts) Triethylene glycol (parts) 5 20 20 20 Pure water Balance Balance Balance Balance Sub-total (parts) 100 100 100 100 Bio-nanofiber Product name CEL-NF CHI-NF CHI-NF CEL-NF (abbreviation) (parts) 1.0 0.25 0.25 1.0 Pure water Balance Balance Balance Balance Total (parts) 250 250 250 250

Preparation Example 1 Ultrasonic Dispersion (US) Aqueous Black Ink (Type 1)

First, 25 parts of pure water was added to 75 parts of the aqueous pigment dispersion (corresponding to a pigment concentration of 8%) produced in Production Example 1 and stirred by using a magnetic stirrer, and then the resultant mixture was filtered with a 1.2 μm membrane filter to produce an ultrasonic dispersion (US) aqueous black ink (Type 1) of Example 1. The physical properties and the like of the prepared ink are described in tables below.

Preparation Example 2 Ultrasonic Dispersion (US) Aqueous Black Ink (Type 2)

First, 50 parts of separately prepared vehicle (mixing ratio by mass: 2-pyrrolidone/triethylene glycol monobutyl ether/glycerin/Surfynol 440/pure water=16/16/6/1/61) was added to 50 parts of the aqueous pigment dispersion (corresponding to a pigment concentration of 8%) produced in Production Example 1 and stirred by using a magnetic stirrer, and then the resultant mixture was filtered with a 1.2 μm membrane filter to produce an ultrasonic dispersion (US) aqueous black ink (Type 2) of Example 14. The physical properties and the like of the prepared ink are described in tables below.

An ultrasonic dispersion (US) aqueous cyan ink (Type 1) was prepared according to Preparation Example 1 or the like described above except that the type of the pigment used, the type of the anionic group-containing organic polymer compound used, and the type and amount of the bio-nanofibers used were changed to those described in each of examples. The physical properties and the like of the prepared ink are described in tables below.

Production Example 5 Method for Producing Kneading Method (PLM) Aqueous Black Pigment Dispersion

In a planetary mixer (ACM04LVTJ-B, manufactured by Aicohsha Manufacturing Co., Ltd.), a mixture (50 parts of carbon black “#960” (manufactured by Mitsubishi Chemical Corporation), 10 parts of anionic group-containing organic polymer compound (resin A), 4.4 parts of a 34% aqueous potassium hydroxide solution, and 50 parts of triethylene glycol) was added, and the mixture was kneaded for 60 minutes at a jacket temperature of 60° C. and a stirring blade rotational speed of 25 rpm (number of revolutions: 80 rpm). Further, the whole of the resultant kneaded product was placed in a domestic mixer (Healthy Mix manufactured by Zojirushi Corporation), and 218.6 parts of pure water was added. After the mixer was hermetically sealed, the resultant mixture was stirred and dissolved for 20 minutes to produce 333 parts of an aqueous mixture MX. In a metal beaker, 53.33 parts of the aqueous mixture MX, 0.3 parts (in terms of solid content) of bio-nanofibers “BiNFi-s Chitosan” (manufactured by Sugino Machine Limited, product name (abbreviation): CHI-NF), and pure water were added so that a total amount was 100 parts, stirred and mixed by a homogenizer (Rotor/Stator manufactured by Silverson Machines Ltd.) at 8000 rpm for 11 minutes, and further diluted with pure water to prepare a kneading method (PLM) aqueous black pigment dispersion (corresponding to a pigment concentration of 8%).

Production Examples 6 to 8 Method for Producing Kneading Method (PLM) Aqueous Cyan Pigment Dispersion

A kneading method (PLM) aqueous cyan pigment dispersion was prepared according to the production method described above except that the type of the pigment used, the type of the anionic group-containing organic polymer compound used, and the type and amount of the bio-nanofibers used were changed to those described in each of examples. Table 3 shows examples of the amount of kneading method (PLM) aqueous pigment dispersion added.

TABLE 3 Production of kneading method (PLM) aqueous pigment dispersion Production Production Production Production Example 5 Example 6 Example 7 Example 8 (Black) (Cyan) (Magenta) (Yellow) Pigment Product name #960 FASTOGEN FASTOGEN Fast Yellow Blue TGR Super 7413 Magenta RY (parts) 50 50 50 50 Anionic group-containing organic 10 15 10 15 polymer compound Resin A (parts) Triethylene glycol (parts) 50 18.75 33.5 27.5 34% aqueous potassium hydroxide 4.4 6.6 4.4 6.6 solution Pure water Balance Balance Balance Balance Aqueous mixture MX (parts) 333 333 333 333 ↓ ↓ ↓ ↓ Aqueous mixture MX (parts) 53.33 53.33 53.33 53.33 Bio-nanofiber Product name CHI-NF CHI-NF CEL-KY CHI-NF (abbreviation) (parts) 0.3 0.3 0.2 0.1 Anionic group- Product name — DN-800H — — containing organic (parts) — 0.4 — — polymer compound Pure water Balance Balance Balance Balance Total (parts) 100 100 100 100

Preparation Example 3 Kneading Method (PLM) Aqueous Black Ink (Type 1)

First, 12.5 parts of pure water was added to 37.5 parts of the aqueous pigment dispersion (corresponding to a pigment concentration of 8%) produced in Production Example 5 and stirred by using a magnetic stirrer, and then the resultant mixture was filtered with a 1.2 μm membrane filter to produce a kneading method (PLM) aqueous black ink (Type 1) of Example 11. The physical properties and the like of the prepared ink are described in tables below.

Preparation Example 4 Kneading Method (PLM) Aqueous Black Ink (Type 2)

First, 25 parts of separately prepared vehicle (mixing ratio by mass: 2-pyrrolidone/triethylene glycol monobutyl ether/glycerin/Surfynol 440/pure water=16/16/6/1/61) was added to 25 parts of the aqueous pigment dispersion (corresponding to a pigment concentration of 8%) produced in Production Example 5 and stirred by using a magnetic stirrer, and then the resultant mixture was filtered with a 1.2 μm membrane filter to produce a kneading method (PLM) aqueous black ink (Type 2) of Example 47. The physical properties and the like of the prepared ink are described in tables below.

A kneading method (PLM) aqueous cyan ink (Type 1) or the like was prepared according to Preparation Example 3 or the like described above except that the type of the pigment used, the type of the anionic group-containing organic polymer compound used, and the type and amount of the bio-nanofibers used were changed to those described in each of examples. The physical properties and the like of the prepared ink are described in tables below.

<Measurement of Ink Physical Properties> (pH Measurement Method)

Measurement (ink temperature of 25° C.) was performed by using MM-60R (manufactured by DKK-TOA Corporation).

(Viscosity Measurement Method)

Measurement (ink temperature of 25° C.) was performed by using Viscometer TV-20 (manufactured by Toki Sangyo Co., Ltd.).

(Measurement Method for Average Particle Diameter)

Measurement (ink temperature of 25° C.) was performed by using a dynamic light scattering Nanotrac particle size analyzer UPA-150EX (manufactured by Nikkiso Co., Ltd.). A volume-based (Mv) median diameter (D₅₀) was used as an average particle diameter.

<Evaluation of Printed Matter> (Measurement of Optical Density (O. D.) Value)

The prepared ink was applied to PPC paper by using wire bar #3. After natural drying for 24 hours, the optical density (O. D.) of a coated product was measured. Measurement was performed by using “Gretag Macbeth Spectro Scan Transmission” (United States X-Rite Inc.), and an average value obtained by measurement of a total 9 points of a 3 by 3 matrix was used as the optical density (O. D.) value of the coated product.

In addition, with respect to improvement in the optical density, the optical density (O. D.) was calculated by a formula below and evaluated based on evaluation criteria below.

(Optical density(O.D.) of sample ink)/(Optical density(O.D.) of reference ink)×100(%)  [Math. 6]

(Determination Criteria)

G: Improvement of 3% or more in optical density

N: No improvement of 3% or more in optical density

(Rubfastness Test)

The prepared ink was applied to glossy paper by using wire bar #3. After natural drying for 24 hours, the coated surface was rubbed with a 45R friction block on which PPC paper for friction was wound using a Gakushin-type rubbing tester (manufactured by Daiei Kagaku Seiki Mfg. Co., Ltd.) under the conditions including a load of 200 g and a number of times of friction of 10. Then, the state of the coated surface was visually observed by three panelists and evaluated according to criteria below.

G: Three panelists evaluated that no damage occurred

N: One or more panelists evaluated that damage occurred

(Marker Resistance Test)

The prepared ink was applied to PPC paper by using wire bar #3. After natural drying for 24 hours, a boundary between an ink coated surface and an uncoated surface on the coated product was traced with a commercial fluorescent pen (Text Liner manufactured by FABER-CASTELL Company). A degree of dirt was visually observed and evaluated according to criteria below (three panelists).

G: By tracing with a fluorescent pen, no staining such as trailing or the like occurred or trailing occurred at a level with no practical problem.

N: By tracing with a fluorescent pen, significant trailing occurred and heavy staining was observed.

<Adaptability for Ink Jet (IJ)>

With respect to discharge properties and printability, an ink jet recording apparatus (ENVY4500 manufactured by Hewlett-Packard Company) having a thermal-type ink jet nozzle was filled with an aqueous ink in a constant-temperature constant-humidity chamber (room temperature 25° C., humidity 50%). Then, printing was continuously performed for 10 minutes on PPC paper as a recording material using a test print pattern (having a character part, a ruled-line part, and a solid part). After continuous printing for 10 minutes, the paper surface was visually observed by three panelists and omission or blurring of the print pattern was evaluated according to criteria below.

G: Neither omission nor blurring in the print pattern was recognized by the three panelists.

M: Omission or blurring in the print pattern was recognized by only one panelist (neither omission nor blurring in the print pattern was recognized by the other two panelists).

N: Omission or blurring in the print pattern was recognized by two or more panelists.

The ink compositions and the ink evaluation results are shown in tables below.

TABLE 4 Production Example 1 Comparative US Example Example Example Example Example Example Aqueous black ink (Type1) dispersion 1 2 3 4 5 1 Dispersion method (US: ultrasonic US US US US US US US dispersion method PLM: kneading method) Composition Black Product name #960 #960 #960 #960 #960 #960 #960 pigment (parts) (solid 8 6 6 6 6 6 6 content) Anionic Name/Product SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 group- name containing (parts) (solid 1.6 1.2 1.2 1.2 1.2 1.2 1.2 organic content) polymer Name/Product — — — — — DN- — compound name 800H (parts) (solid — — — — — 0.15 — content) Bio- Product name CEL-NF CEL-NF CEL-KY CEL-KY CHI-NF CHI-NF — nanofiber (abbreviation) (parts) 0.4 0.3 0.075 0.6 0.225 0.6 — Triethylene glycol (parts) 2 1.5 1.5 1.5 1.5 1.5 1.5 Pure water Balance Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 100 Physical pH 10.4 10.3 10.2 10.4 10.2 10.3 10.3 properties Average particle 85 78 79 78 81 83 81 diameter D50/nm Initial viscosity (mPa · s) — 19.9 6.3 63.2 15.5 89.2 1.7 Optical Measured — 1.43 1.38 1.44 1.42 1.44 1.34 density value Improvement — 107% 103% 107% 106% 107% (reference) rate Determination — G G G G G — Rubfastness — G G G G G N

TABLE 5 Comparative Example Example Example Example Example Example Aqueous black ink (Type1) 6 7 8 9 10 2 Dispersion method (US: ultrasonic US US US US US US dispersion method PLM: kneading method) Composition Black Product name #960 #960 #960 #960 #960 #960 pigment (parts) (solid 6 6 6 6 6 6 content) Anionic Name/Product UR-1 UR-1 UR-1 UR-1 UR-1 UR-1 group- name containing (parts) (solid 1.2 1.2 1.2 1.2 1.2 1.2 organic content) polymer Name/Product — CMC DN-100L — CMC — compound name 1390 1390 (parts) (solid — 0.1 0.3 — 0.2 — content) Bio- Product name CHI-NF CHI-NF CHI-NF CEL-NF CEL-KY — nanofiber (abbreviation) (parts) 0.075 0.3 0.3 0.3 0.3 — Triethylene glycol (parts) 1.5 1.5 1.5 1.5 1.5 1.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 9.4 9.5 9.5 8.9 8.9 8.9 properties Average particle diameter 124 123 123 110 122 125 D50/nm Initial viscosity (mPa · s) 8.2 18.2 11.6 29.5 9.8 2.3 Optical Measured 1.38 1.42 1.42 1.41 1.43 1.33 density value Improvement 103% 107% 107% 106% 107% (reference) rate Determination G G G G G — Rubfastness G G G G G N

TABLE 6 Production Example 5 Comparative PLM Example Example Example Example Aqueous black ink (Type1) Dispersion 11 12 13 3 Dispersion method (US: ultrasonic dispersion PLM PLM PLM PLM PLM method PLM: kneading method) Composition Black pigment Product name #960 #960 #960 #960 #960 (parts) (solid 8 6 6 6 6 content) Anionic Name/Product Resin A Resin A Resin A Resin A Resin A group- name containing (parts) (solid 1.6 1.2 1.2 1.2 1.2 organic content) polymer Name/Product — — DN-800H — — compound name (parts) (solid — — 0.15 — — content) Bio-nanofiber Product name CHI-NF CHI-NF CHI-NF CEL-KY — (abbreviation) (parts) 0.3 0.225 0.225 0.6 — Triethylene glycol (parts) 8 6 6 6 6 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical pH 9.8 9.6 10.0 10.1 10.1 properties Average particle diameter 108 104 106 111 116 D50/nm Initial viscosity (mPa · s) — 10.2 10.2 52.2 1.9 Optical Measured value — 1.27 1.29 1.34 1.19 density Improvement — 107% 108% 113% (reference) rate Determination — G G G — Rubfastness — G G G N

TABLE 7 Production Example 1 US Example Example Example Example Example Aqueous black ink (Type2) dispersion 14 15 16 17 18 Dispersion method (US: ultrasonic US US US US US US dispersion method PLM: kneading method) Composition Black pigment Product name #960 #960 #960 #960 #960 #960 (parts) (solid 8 4 4 4 4 4 content) Anionic Name/Product SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 group- name containing (parts) (solid 1.6 0.8 0.8 0.8 0.8 0.8 organic content) polymer Name/Product — — — — — — compound name (parts) (solid — — — — — — content) Bio-nanofiber Product name CEL-NF CEL-NF CEL-KY CEL-KY CEL-KY CEL-KY (abbreviation) (parts) 0.4 0.2 0.2 0.1 0.05 0.3 2-pyrrolidone (parts) — 8 8 8 8 8 Triethylene glycol — 8 8 8 8 8 Glycerin (parts) — 3 3 3 3 3 Triethylene glycol (parts) 2 1 1 1 1 1 Surfynol 440(parts) — 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 10.4 9.3 9.3 9.3 9.2 9.3 properties Average particle diameter D50/nm 85 81 82 82 83 81 Initial viscosity (mPa · s) — 3.7 16.8 8.8 4.5 28.1 Optical Measured value — 1.11 1.07 1.05 1.04 1.11 density Improvement rate — 112% 108% 106% 105% 112% Determination — G G G G G Rubfastness — G G G G G Maker resistance — G G G G G Ink jet adaptability — G G G G M Example Example Example Example Example Example Aqueous black ink (Type2) 19 20 21 22 23 24 Dispersion method (US: ultrasonic US US US US US US dispersion method PLM: kneading method) Composition Black pigment Product name #960 #960 #960 #960 #960 #960 (parts) (solid 4 4 4 4 4 4 content) Anionic Name/Product SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 group- name containing (parts) (solid 0.8 0.8 0.8 0.8 0.8 0.8 organic content) polymer Name/Product — CMC DN-800H CMC — — compound name 1390 1240 (parts) (solid — 0.2 0.2 0.2 — — content) Bio-nanofiber Product name CEL-KY CEL-KY CEL-KY CEL-KY CHI-NF CHI-NF (abbreviation) (parts) 0.4 0.2 0.2 0.2 0.05 0.15 2-pyrrolidone (parts) 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 Triethylene glycol (parts) 1 1 1 1 1 1 Surfynol 440(parts) 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 9.4 9.2 9.1 9.3 9.2 9.2 properties Average particle diameter D50/nm 81 84 83 85 88 88 Initial viscosity (mPa · s) 41.3 13.7 12.0 9.6 4.8 20.1 Optical Measured value 1.15 1.08 1.07 1.06 1.07 1.12 density Improvement rate 116% 109% 108% 107% 108% 113% Determination G G G G G G Rubfastness G G G G G G Maker resistance G G G G G G Ink jet adaptability M G G G G M

TABLE 8 Example Example Example Example Example Example Example Aqueous black ink (Type2) 25 26 27 28 29 30 31 Dispersion method (US: ultrasonic dispersion US US US US US US US method PLM: kneading method) Composition Black Product name #960 #960 #960 #960 #960 #960 #960 pigment (parts) (solid content) 4 4 4 4 4 4 4 Anionic Name/Product name SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 group- (parts) (solid content) 0.8 0.8 0.8 0.8 0.8 0.8 0.8 containing Name/Product name DN-800H DN-100L DN-10L CMC DN-100L DN-10L DN-800H organic 1390 polymer (parts) (solid content) 0.15 0.15 0.15 0.1 0.2 0.1 0.3 compound Bio-nanofiber Product name CHI-NF CHI-NF CHI-NF CHI-NF CHI-NF CHI-NF CHI-NF (abbreviation) (parts) 0.15 0.15 0.15 0.1 0.1 0.2 0.15 2-Pyrrolidone (parts) 8 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 3 Triethylene glycol (parts) 1 1 1 1 1 1 1 Surfynol 440 (parts) 0.5 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 100 Physical pH 9.4 9.5 9.4 9.2 9.2 9.2 7.8 properties Average particle diameter D50/nm 89 86 85 88 91 88 132 Initial viscosity (mPa · s) 5.9 5.5 4.6 8.4 5.7 6.9 4.8 Optical Measured value 1.09 1.07 1.04 1.10 1.09 1.10 1.07 density Improvement rate 110% 108% 105% 111% 110% 111% 108% Determination G G G G G G G Rubfastness G G G G G G G Marker resistance G G G G G G G Ink jet adaptability G G G G G G G Comparative Comparative Comparative Example Example Example Example Example Aqueous black ink (Type2) 32 33 4 5 6 Dispersion method (US: ultrasonic dispersion US US US US US method PLM: kneading method) Composition Black Product name #960 #960 #960 #960 #960 pigment (parts) (solid content) 4 4 4 4 4 Anionic Name/Product name SA-1 SA-1 SA-1 SA-1 SA-1 group- (parts) (solid content) 0.8 0.8 0.8 0.8 0.8 containing Name/Product name DN-800H DN-800H CMC DN-800H — organic 1390 polymer (parts) (solid content) 0.15 0.15 0.2 0.2 — compound Bio-nanofiber Product name CHI-NF CHI-NF — — — (abbreviation) (parts) 0.3 0.4 — — — 2-Pyrrolidone (parts) 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 Triethylene glycol (parts) 1 1 1 1 1 Surfynol 440 (parts) 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical pH 9.4 9.3 9.4 9.2 9.3 properties Average particle diameter D50/nm 89 90 88 97 88 Initial viscosity (mPa · s) 14.2 18.8 6.7 5.1 2.3 Optical Measured value 1.14 1.16 1.02 1.01 0.99 density Improvement rate 115% 117% 103% 102% (Reference) Determination G G G N — Rubfastness G G N N N Marker resistance G G N N N Ink jet adaptability G M G G G

TABLE 9 Example Example Example Example Example Example Aqueous black ink (Type2) 34 35 36 37 38 39 Dispersion method (US: ultrasonic US US US US US US dispersion method PLM: kneading method) Composition Black pigment Product name #960 #960 #960 #960 #960 #960 (parts) (solid 4 4 4 4 4 4 content) Anionic group- Name/Product name UR-1 UR-1 UR-1 UR-1 UR-1 UR-1 containing (parts) (solid 0.8 0.8 0.8 0.8 0.8 0.8 organic content) polymer Name/Product name — — — — CMC — compound 1390 (parts) (solid — — — — 0.2 — content) Bio-nanofiber Product name CEL-KY CEL-KY CEL-KY CEL-NF CEL-KY CHI-NF (abbreviation) (parts) 0.2 0.1 0.05 0.2 0.2 0.05 2-Pyrrolidone (parts) 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 Triethylene glycol (parts) 1 1 1 1 1 1 Surfynol 440 (parts) 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 7.5 7.4 7.5 7.4 7.4 7.8 properties Average particle diameter D50/nm 119 124 128 117 130 132 Initial viscosity (mPa · s) 17.3 10.2 5.1 4.0 3.6 4.1 Optical density Measured value 1.03 1.01 0.99 1.04 1.05 1.00 Improvement rate 110% 107% 105% 111% 112% 106% Determination G G G G G G Rubfastness G G G G G G Maker resistance G G G G G G Ink jet adaptability G G G G G G Example Example Example Example Example Example Aqueous black ink (Type2) 40 41 42 43 44 45 Dispersion method (US: ultrasonic US US US US US US dispersion method PLM: kneading method) Composition Black pigment Product name #960 #960 #960 #960 #960 #960 (parts) (solid 4 4 4 4 4 4 content) Anionic group- Name/Product name UR-1 UR-1 UR-1 UR-1 UR-1 UR-1 containing (parts) (solid 0.8 0.8 0.8 0.8 0.8 0.8 organic content) polymer Name/Product name — DN-800H DN-100L DN-10L CMC DN-100L compound 1390 (parts) (solid — 0.15 0.15 0.15 0.1 0.3 content) Bio-nanofiber Product name CHI-NF CHI-NF CHI-NF CHI-NF CHI-NF CHI-NF (abbreviation) (parts) 0.15 0.15 0.15 0.15 0.2 0.2 2-Pyrrolidone (parts) 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 Triethylene glycol (parts) 1 1 1 1 1 1 Surfynol 440 (parts) 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 7.8 7.9 7.8 7.9 7.9 7.9 properties Average particle diameter D50/nm 132 132 133 130 131 131 Initial viscosity (mPa · s) 20.2 5.9 5.6 4.7 15.4 9.3 Optical density Measured value 1.03 1.06 1.07 1.02 1.08 1.08 Improvement rate 110% 113% 114% 109% 115% 115% Determination G G G G G G Rubfastness G G G G G G Maker resistance G G G G G G Ink jet adaptability M G G G M G

TABLE 10 Production Comparative Comparative Example 5 Example Example Example PLM Example Example Aqueous black ink (Type2) 46 7 8 Dispersion 47 48 Dispersion method (US: ultrasonic dispersion method US US US PLM PLM PLM PLM: kneading method) Composition Black Product name #960 #960 #960 #960 #960 #960 pigment (parts) (solid content) 4 4 4 8 4 4 Anionic Name/Product name UR-1 UR-1 UR-1 Resin A Resin A Resin A group- (parts) (solid content) 0.8 0.8 0.8 1.6 0.8 0.8 containing Name/Product name DN- CMC — — — — organic 800H 1390 polymer (parts) (solid content) 0.15 0.2 — — — — compound Bio- Product name- CHI-NF CHI-NF CHI-NF CEL-KY nanofiber abbreviation (parts) 0.4 — — 0.3 0.15 0.2 2-Pyrrolidone (parts) 8 8 8 — 8 8 Triethylene glycol 8 8 8 — 8 8 Glycerin (parts) 3 3 3 — 3 3 Triethylene glycol (parts) 1 1 1 8 4 4 Surfynol 440(parts) 0.5 0.5 0.5 — 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 8.0 7.3 7.4 9.8 9.0 9.5 properties Average particle diameter D50/nm 138 91 133 108 87 96 Initial viscosity (mPa · s) 18.5 4.2 14.5 — 20.2 7.3 Optical Measured value 1.09 0.96 0.94 — 1.05 1.01 density Improvement rate 116% 102% (Reference) — 112% 107% Determination G N — — G G Rubfastness G N N — G G Maker resistance G N N — G G Ink jet adaptability M G G — M G Example Example Example Example Example Example Aqueous black ink (Type2) 49 50 51 52 53 54 Dispersion method (US: ultrasonic dispersion method PLM PLM PLM PLM PLM PLM PLM: kneading method) Composition Black Product name #960 #960 #960 #960 #960 #960 pigment (parts) (solid content) 4 4 4 4 4 4 Anionic Name/Product name Resin A Resin A Resin A Resin A Resin A Resin A group- (parts) (solid content) 0.8 0.8 0.8 0.8 0.8 0.8 containing Name/Product name — — — — — CMC organic 1390 polymer (parts) (solid content) — — — — — 0.2 compound Bio- Product name- CEL-KY CEL-KY CEL-KY CEL-KY CEL-NF CEL-KY nanofiber abbreviation (parts) 0.1 0.05 0.3 0.4 0.2 0.2 2-Pyrrolidone (parts) 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 Triethylene glycol (parts) 4 4 4 4 4 4 Surfynol 440(parts) 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 9.5 9.4 9.4 9.5 9.5 9.4 properties Average particle diameter D50/nm 96 97 95 93 92 94 Initial viscosity (mPa · s) 4.8 3.2 16.8 29.3 4.5 6.9 Optical Measured value 1.00 0.99 1.04 1.10 1.05 1.01 density Improvement rate 106% 105% 111% 117% 112% 107% Determination G G G G G G Rubfastness G G G G G G Maker resistance G G G G G G Ink jet adaptability G G M M G G

TABLE 11 Example Example Example Example Example Aqueous black ink (Type2) 55 56 57 58 59 Dispersion method (US: ultrasonic dispersion method PLM PLM PLM PLM PLM PLM: kneading method) Composition Black pigment Product name #960 #960 #960 #960 #960 (parts) (solid content) 4 4 4 4 4 Anionic group-containing Name/Product name Resin A Resin A Resin A Resin A Resin A organic polymer compound (parts) (solid content) 0.8 0.8 0.8 0.8 0.8 Name/Product name DN-800H DN-800H DN-100L DN-10L CMC 1390 (parts) (solid content) 0.2 0.15 0.15 0.15 0.1 Bio-nanofiber Product name- CEL-KY CHI-NF CHI-NF CHI-NF CHI-NF abbreviation (parts) 0.2 0.15 0.15 0.15 0.15 2-Pyrrolidone (parts) 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 Triethylene glycol (parts) 4 4 4 4 4 Surfynol 440(parts) 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical properties pH 9.3 9.4 9.4 9.5 9.4 Average particle diameter D50/nm 95 89 89 87 85 Initial viscosity (mPa · s) 5.9 6.0 5.6 4.7 15.5 Optical density Measured value 1.00 1.08 1.02 1.01 1.05 Improvement rate 106% 115% 109% 107% 112% Determination G G G G G Rubfastness G G G G G Maker resistance G G G G G Ink jet adaptability G G G G M Comparative Comparative Comparative Example Example Example Example Aqueous black ink (Type2) 60 9 10 11 Dispersion method (US: ultrasonic dispersion method PLM PLM PLM PLM PLM: kneading method) Composition Black pigment Product name #960 #960 #960 #960 (parts) (solid content) 4 4 4 4 Anionic group-containing Name/Product name Resin A Resin A Resin A Resin A organic polymer compound (parts) (solid content) 0.8 0.8 0.8 0.8 Name/Product name DN-800H CMC DN-800H — 1390 (parts) (solid content) 0.15 0.2 0.2 — Bio-nanofiber Product name- CHI-NF — — — abbreviation (parts) 0.4 — — — 2-Pyrrolidone (parts) 8 8 8 8 Triethylene glycol 8 8 8 8 Glycerin (parts) 3 3 3 3 Triethylene glycol (parts) 4 4 4 4 Surfynol 440(parts) 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Total (parts) 100 100 100 100 Physical properties pH 9.5 9.6 9.4 9.5 Average particle diameter D50/nm 97 97 103 97 Initial viscosity (mPa · s) 18.6 4.2 3.9 2.8 Optical density Measured value 1.15 0.97 0.97 0.94 Improvement rate 122% 103% 103% (Reference) Determination G G G — Rubfastness G N N N Maker resistance G N N N Ink jet adaptability M G G G

TABLE 12 Comparative Comparative Example Example Example Example Example Example Aqueous black ink (Type2) 61 62 63 64 12 13 Dispersion method (US: ultrasonic dispersion method Self- Self- Self- Self- Self-dispersion Self- PLM: kneading method) dispersion dispersion dispersion dispersion type dispersion type type type type type Composition Black pigment Product name CAB-O- CAB-O- CAB-O- CAB-O- CAB-O- CAB-O- JET JET JET JET JET JET 400 400 400 400 400 400 (parts) (solid content) 4 4 4 4 4 4 Anionic group- Name/Product name — — — — — — containing organic (parts) (solid content) — — — — — — polymer Name/Product name CMC DN-800H CMC DN-800H — DN-800H compound 1390 1390 (parts) (solid content) 0.2 0.2 0.2 0.2 — 0.2 Bio-nanofiber Product name- CEL-NF CEL-NF CEL-KY CEL-KY CEL-NF — abbreviation (parts) 0.2 0.2 0.2 0.2 0.5 — 2-Pyrrolidone (parts) 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 Triethylene glycol (parts) 1 1 1 1 1 1 Surfynol 440(parts) 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 8.3 8.0 8.2 8.1 8.4 8.2 properties Average particle diameter D50/nm 131 148 131 139 386 139 Initial viscosity (mPa · s) 6.6 4.9 8.3 7.2 88.3 6.9 Optical density Measured value 1.32 1.29 1.22 1.20 1.58 1.10 Improvement rate 126% 123% 116% 114% 150% 105% Determination G G G G G G Rubfastness G G G G G N Maker resistance G G G G G N Ink jet adaptability G G G G N G Comparative Comparative Example Example Example Example Aqueous black ink (Type2) 14 65 66 12 Dispersion method (US: ultrasonic dispersion method Self-dispersion Self- Self- Self- PLM: kneading method) type dispersion dispersion dispersion type type type Composition Black pigment Product name CAB-O- SENSI SENSI SENSI JET JET Black JET Black JET Black 400 SDP SDP SDP 100 100 100 (parts) (solid content) 4 4 4 4 Anionic group- Name/Product name — — — — containing organic (parts) (solid content) — — — — polymer Name/Product name — CMC CMC — compound 1390 1390 (parts) (solid content) — 0.2 0.2 — Bio-nanofiber Product name- — CEL-NF CEL-KY — abbreviation (parts) — 0.2 0.2 — 2-Pyrrolidone (parts) 8 8 8 8 Triethylene glycol 8 8 8 8 Glycerin (parts) 3 3 3 3 Triethylene glycol (parts) I 1 1 1 Surfynol 440(parts) 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Total (parts) 100 100 100 100 Physical pH 8.3 8.1 8.1 7.9 properties Average particle diameter D50/nm 131 118 121 117 Initial viscosity (mPa · s) 2.1 8.8 8.8 2.1 Optical density Measured value 1.05 1.29 1.25 1.15 Improvement rate (Reference) 112% 109% (Reference) Determination — G G — Rubfastness N G G N Maker resistance N G G N Ink jet adaptability G G G G

TABLE 13 Production Example 2 US Example Example Example Example Example Aqueous cyan ink (Type1) Dispersion 67 68 69 70 71 Dispersion method (US: ultrasonic dispersion US US US US US US method PLM: kneading method) Composition Cyan pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR (parts) (solid 8 6 6 6 6 6 content) Anionic group- Name/Product SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 containing name organic polymer (parts) (solid 1.6 1.2 1.2 1.2 1.2 1.2 compound content) Name/Product — — — — CMC DN-800H name 1390 (parts) (solid — — — — 0.3 0.225 content) Bio-nanofiber Product name CHI-NF CHI-NF CEL-KY CEL-NF CEL-NF CHI-NF (abbreviation) (parts) (solid 0.1 0.075 0.3 0.15 0.3 0.6 content) Triethylene glycol (parts) 8 6 6 6 6 6 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 9.6 9.4 9.5 9.6 9.5 9.6 properties Average particle diameter D50/nm 96 93 94 93 94 91 Initial viscosity (mPa · s) — 3.9 13.8 5.2 18.1 63.4 Optical density Measured value — 1.27 1.26 1.23 1.28 1.36 Improvement rate — 108% 107% 105% 109% 115% Determination — G G G G G Rubfastness — G G G G G Comparative Comparative Example Example Example Example Example Example Aqueous cyan ink (Type1) 13 72 73 74 75 14 Dispersion method (US: ultrasonic dispersion US US US US US US method PLM: kneading method) Composition Cyan pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR (parts) (solid 6 6 6 6 6 6 content) Anionic group- Name/Product SA-1 UR-1 UR-1 UR-1 UR-1 UR-1 containing name organic polymer (parts) (solid 1.2 1.2 1.2 1.2 1.2 1.2 compound content) Name/Product — — DN-800H DN-100L — — name (parts) (solid — — 0.225 0.225 — — content) Bio-nanofiber Product name CHI-NF CHI-NF CHI-NF CEL-KY (abbreviation) (parts) (solid — 0.225 0.225 0.6 0.3 — content) Triethylene glycol (parts) 6 6 6 6 6 6 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 9.6 8.9 8.8 8.9 8.9 9.6 properties Average particle diameter D50/nm 91 120 125 121 99 91 Initial viscosity (mPa · s) 1.8 6.2 9.4 59.1 19.3 2.4 Optical density Measured value 1.17 1.23 1.28 1.34 1.21 1.09 Improvement rate (Reference) 113% 118% 123% 111% (Reference) Determination — G G G G — Rubfastness N G G G G N

TABLE 14 Production Example 6 Comparative PLM Example Example Example Example Aqueous cyan ink (Type1) Dispersion 76 77 15 78 Dispersion method (US: ultrasonic dispersion method PLM PLM PLM PLM Self- PLM: kneading method) dispersion type Composition Cyan pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN CAB-O-JET Blue TGR Blue TGR Blue TGR Blue TGR 450C (parts) (solid content) 8 6 6 6 6 Anionic group-containing Name/Product name Resin A Resin A Resin A Resin A — organic polymer (parts) (solid content) 2.4 1.8 1.8 1.8 — compound Name/Product name DN-800H DN-800H DN-800H — CMC 1390 (parts) (solid content) 0.4 0.3 0.225 — 0.3 Bio-nanofiber Product name CHI-NF CHI-NF CHI-NF CEL-NF (abbreviation) (parts) (solid content) 0.3 0.225 0.6 — 0.3 Triethylene glycol (parts) 3 2.25 2.25 2.25 1.5 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical pH 9.9 9.8 9.9 9.9 9.8 properties Average particle diameter D50/nm 95 90 95 89 86 Initial viscosity (mPa · s) — 13.6 52.8 1.5 35.1 Optical density Measured value — 1.25 1.32 1.16 1.39 Improvement rate — 107% 114% (Reference) 115% Determination — G G — G Rubfastness — G G N G Comparative Example Example Example Example Aqueous cyan ink (Type1) 79 80 81 16 Dispersion method (US: ultrasonic dispersion method Self- Self- Self- Self- PLM: kneading method) dispersion dispersion dispersion dispersion type type type type Composition Cyan pigment Product name CAB-O-JET CAB-O-JET CAB-O- CAB-O-JET 450C 450C JET 450C 450C (parts) (solid content) 6 6 6 6 Anionic group-containing Name/Product name — — — — organic polymer (parts) (solid content) — — — — compound Name/Product name DN-800H CMC DN-800H — 1390 (parts) (solid content) 0.3 0.3 0.3 — Bio-nanofiber Product name CEL-NF CEL-KY CEL-KY (abbreviation) (parts) (solid content) 0.3 0.3 0.3 — Triethylene glycol (parts) 1.5 1.5 1.5 1.5 Pure water Balance Balance Balance Balance Total (parts) 100 100 100 100 Physical pH 9.4 9.8 9.5 9.7 properties Average particle diameter D50/nm 83 89 90 84 Initial viscosity (mPa · s) 15.2 23.5 9.9 1.2 Optical density Measured value 1.34 1.29 1.28 1.21 Improvement rate 111% 107% 106% (Reference) Determination G G G — Rubfastness G G G N

TABLE 15 Production Example 2 US Example Example Example Example Example Aqueous cyan ink (Type2) Dispersion 82 83 84 85 86 Dispersion method (US: ultrasonic dispersion US US US US US US method PLM: kneading method) Composition Cyan pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR (parts) (solid 8 4 4 4 4 4 content) Anionic Name/Product name SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 group- (parts) (solid 1.6 0.8 0.8 0.8 0.8 0.8 containing content) organic Name/Product name — — — — CMC DN-800H polymer 1390 compound (parts) (solid — — — — 0.2 0.2 content) Bio-nanofiber Product name CHI-NF CHI-NF CEL-KY CEL-KY CEL-KY CEL-KY (abbreviation) (parts) (solid 0.1 0.05 0.2 0.1 0.2 0.2 content) 2-Pyrrolidone (parts) — 8 8 8 8 8 Triethylene glycol — 8 8 8 8 8 Glycerin (parts) — 3 3 3 3 3 Triethylene glycol (parts) 8 4 4 4 4 4 Surfynol 440(parts) — 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 9.6 8.8 8.9 9.0 8.9 8.9 properties Average particle diameter D50/nm 96 95 96 95 96 96 Initial viscosity (mPa · s) — 4.5 9.7 5.1 8.8 9.7 Optical Measured value — 1.05 1.04 1.02 1.06 1.04 density Improvement rate — 108% 107% 105% 109% 107% Determination — G G G G G Rubfastness — G G G G G Ink jet adaptability — G G G G G Example Example Example Example Example Example Aqueous cyan ink (Type2) 87 88 89 90 91 92 Dispersion method (US: ultrasonic dispersion US US US US US US method PLM: kneading method) Composition Cyan pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR (parts) (solid 4 4 4 4 4 4 content) Anionic Name/Product name SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 group- (parts) (solid 0.8 0.8 0.8 0.8 0.8 0.8 containing content) organic Name/Product name — DN-800H DN-10L DN-100L CMC DN-100L polymer 1390 compound (parts) (solid — 0.15 0.15 0.2 0.1 0.15 content) Bio-nanofiber Product name CHI-NF HI-NF CHI-NF CHI-NF CHI-NF CHI-NF (abbreviation) (parts) (solid 0.15 0.15 0.15 0.1 0.15 0.3 content) 2-Pyrrolidone (parts) 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 Triethylene glycol (parts) 4 4 4 4 4 4 Surfynol 440(parts) 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 8.8 9.2 9.3 9.0 9.0 9.0 properties Average particle diameter D50/nm 95 92 93 95 95 95 Initial viscosity (mPa · s) 16.8 7.9 7.8 8.3 15.2 11.7 Optical Measured value 1.10 1.07 1.05 1.08 1.08 1.10 density Improvement rate 113% 110% 108% 111% 111% 113% Determination G G G G G G Rubfastness G G G G G G Ink jet adaptability M G G G M G

TABLE 16 Comparative Example Example Example Example Example Aqueous cyan ink (Type2) 93 17 94 95 96 Dispersion method (US: ultrasonic dispersion method US US US US US PLM: kneading method) Composition Cyan pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR (parts) (solid content) 4 4 4 4 4 Anionic group-containing Name/Product name SA-1 SA-1 UR-1 UR-1 UR-1 organic polymer compound (parts) (solid content) 0.8 0.8 0.8 0.8 0.8 Name/Product name DN-800H — — — DN-800H (parts) (solid content) 0.15 — — — 0.15 Bio-nanofiber Product name CHI-NF — CEL-KY CHI-NF CHI-NF (abbreviation) (parts) (solid content) 0.4 — 0.2 0.15 0.15 2-Pyrrolidone (parts) 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 Triethylene glycol (parts) 4 4 4 4 4 Surfynol 440(parts) 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical pH 9.0 9.0 8.3 8.3 8.2 properties Average particle diameter D90/nm 93 93 101 122 127 Initial viscosity (mPa · s) 17.3 2.1 8.9 7.7 18.8 Optical density Measured value 1.12 0.97 1.00 1.02 1.06 Improvement rate 115% (Reference) 111% 113% 118% Determination G — G G G Rubfastness G N G G G Ink jet adaptability M G G G M Comparative Example Example Example Example Aqueous cyan ink (Type2) 97 98 99 18 Dispersion method (US: ultrasonic dispersion method US US US US PLM: kneading method) Composition Cyan pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN Blue TGR Blue TGR Blue TGR Blue TGR (parts) (solid content) 4 4 4 4 Anionic group-containing Name/Product name UR-1 UR-1 UR-1 UR-1 organic polymer compound (parts) (solid content) 0.8 0.8 0.8 0.8 Name/Product name DN-10L CMC DN-100L — 1390 (parts) (solid content) 0.15 0.1 0.15 — Bio-nanofiber Product name CHI-NF CHI-NF CHI-NF — (abbreviation) (parts) (solid content) 0.15 0.15 0.4 — 2-Pyrrolidone (parts) 8 8 8 8 Triethylene glycol 8 8 8 8 Glycerin (parts) 3 3 3 3 Triethylene glycol (parts) 4 4 4 4 Surfynol 440(parts) 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Total (parts) 100 100 100 100 Physical pH 8.4 8.3 8.3 9.0 properties Average particle diameter D90/nm 121 122 123 93 Initial viscosity (mPa · s) 12.4 5.8 17.1 2.5 Optical density Measured value 1.04 1.01 1.11 0.90 Improvement rate 116% 112% 123% (Reference) Determination G G G — Rubfastness G G G N Ink jet adaptability G G M G

TABLE 17 Production Example 6 Comparative Comparative PLM Example Example Example Example Example Example Example Example Example Example Example Aqueous cyan ink (Type2) Dispersion 100 101 102 103 104 105 106 107 108 19 20 Dispersion method (US: ultrasonic dispersion PLM PLM PLM PLM PLM PLM PLM PLM PLM PLM PLM PLM method PLM: kneading method) Composition Cyan Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN pigment Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR Blue TGR (parts) (solid 8 4 4 4 4 4 4 4 4 4 4 4 content) Anionic Name/Product Resin A Resin A Resin A Resin A Resin A Resin A Resin A Resin A Resin A Resin A Resin A Resin A group- name containing (parts) (solid 2.4 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.2 organic content) polymer Name/Product DN-800H DN-800H — — DN-800H CMC DN-100L CMC DN-100L DN-800H DN-800H — compound name 1390 1390 (parts) (solid 0.4 0.2 — — 0.2 0.1 0.15 0.1 0.15 0.15 0.2 — content) Bio- Product name CHI-NF CHI-NF CEL-KY CEL-KY CEL-KY CEL-KY CHI-NF CHI-NF CHI-NF CHI-NF — — nanofiber (abbreviation) (parts) (solid 0.3 0.15 0.2 0.1 0.2 0.1 0.2 0.15 0.3 0.4 — — content) 2-Pyrrolidone (parts) — 8 8 8 8 8 8 8 8 8 8 8 Triethylene glycol — 8 8 8 8 8 8 8 8 8 8 8 Glycerin (parts) — 3 3 3 3 3 3 3 3 3 3 3 Triethylene glycol (parts) 3 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 Surfynol 440(parts) — 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 100 100 100 100 100 100 Physical pH 9.9 9.2 9.3 9.3 9.1 9.1 9.3 9.0 8.8 9.3 9.1 9.3 properties Average particle 95 92 92 92 93 93 93 96 96 97 90 91 diameter D50/nm Initial viscosity (mPa · s) — 9.9 6.6 3.9 25.6 14.8 7.9 9.1 16.1 17.4 12.8 2.5 Optical Measured value — 1.03 1.00 0.98 0.99 0.99 1.02 1.01 1.06 1.09 0.97 0.95 density Improvement rate — 108% 105% 103% 104% 104% 107% 106% 112% 115% 102% (Reference) Determination — G G G G G G G G G N — Rubfastness — G G G G G G G G G N N Ink jet adaptability — G G G M G G G M M G G

TABLE 18 Comparative Comparative Comparative Example Example Example Example Example Example Example Aqueous cyan ink (Type 2) 109 110 111 112 21 22 23 Dispersion method (US: ultrasonic dispersion method Self- Self- Self- Self- Self- Self- Self- PLM: kneading method) dispersion dispersion dispersion dispersion dispersion dispersion dispersion type type type type type type type Composition Cyan pigment Product name CAB-O- CAB-O- CAB-O- CAB-O- CAB-O- CAB-O- CAB-O- JET JET JET JET JET JET JET 450C 450C 450C 450C 450C 450C 450C (parts) (solid content) 4 4 4 4 4 4 4 Anionic Name/Product name — — — — — — — group-containing (parts) (solid content) — — — — — — — organic polymer Name/Product name CMC DN-800H CMC DN-800H — CMC — compound 1390 1390 1390 (parts) (solid content) 0.2 0.2 0.2 0.2 — 0.2 — Bio-nanofiber Product name CEL-NF CEL-NF CEL-KY CEL-KY CEL-NF — — (abbreviation) (parts) (solid content) 0.2 0.2 0.2 0.2 0.5 — — 2-Pyrrolidone (parts) 8 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 3 Triethylene glycol (parts) 1 1 1 1 1 1 1 Surfynol 440 (parts) 0.5 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 100 Physical pH 9.2 8.8 9.2 8.9 9.2 9.0 9.1 properties Average particle diameter D50/nm 88 85 91 92 203 86 86 Initial viscosity (mPa · s) 13.4 9.7 10.7 9.9 456.0 6.9 2.0 Optical density Measured value 1.15 1.11 1.07 1.06 1.40 1.01 1.00 Improvement rate 115% 111% 107% 106% 140% 101% (Reference) Determination G G G G G N — Rubfastness G G G G G N N Ink jet adaptability M G G G N G G

TABLE 19 Production Example 3 Example Example Example Example Aqueous magenta ink (Type 1) US Dispersion 113 114 115 116 Dispersion method (US: ultrasonic dispersion US US US US US method) Composition Magenta Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN pigment Super Magenta Super Magenta Super Magenta Super Magenta Super Magenta RY RY RY RY RY (parts) (solid 8 6 6 6 6 content) Anionic group- Name/Product SA-1 SA-1 SA-1 SA-1 SA-1 containing name organic (parts) (solid 2.4 1.8 1.8 1.8 1.8 polymer content) compound Name/Product — — — CMC DN-800H name 1390 (parts) (solid — — — 0.3 0.3 content) Bio-nanofiber Product name CHI- CHI- CEL- CEL-NF CEL-KY (abbreviation) NF NF NF (parts) (solid 0.1 0.075 0.15 0.15 0.15 content) Triethylene glycol (parts) 8 6 6 6 6 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical pH 9.9 9.6 9.9 10.0 10.0 properties Average particle diameter D50/nm 96 90 105 105 104 Initial viscosity (mPa · s) — 3.1 34.5 11.7 17.1 Optical density Measured value — 1.20 1.19 1.35 1.32 Improvement rate — 104% 103% 117% 115% Determination — G G G G Rubfastness — G G G G Comparative Comparative Example Example Example Example Example Aqueous magenta ink (Type 1) 117 24 118 119 25 Dispersion method (US: ultrasonic dispersion US US US US US method) Composition Magenta Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN pigment Super Magenta Super Magenta Super Magenta Super Magenta Super Magenta RY RY RY RY RY (parts) (solid 6 6 6 6 6 content) Anionic group- Name/Product SA-1 SA-1 UR-1 UR-1 UR-1 containing name organic (parts) (solid 1.8 1.8 1.8 1.8 1.8 polymer content) compound Name/Product DN-800H — DN-10L DN-100L — name (parts) (solid 0.225 — 0.15 0.225 — content) Bio-nanofiber Product name CHI-NF — CHI-NF CHI-NF — (abbreviation) (parts) (solid 0.6 — 0.225 0.6 — content) Triethylene glycol (parts) 6 6 6 6 6 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical pH 9.8 10.1 9.3 9.2 8.6 properties Average particle diameter D50/nm 94 104 96 103 105 Initial viscosity (mPa · s) 49.3 1.4 11.6 56.6 2.3 Optical density Measured value 1.34 1.15 1.16 1.19 1.07 Improvement rate 117% (Reference) 109% 111% (Reference) Determination G — G G — Rubfastness G N G G G

TABLE 20 Production Example 7 Comparative PLM Example Example Example Example Example Aqueous magenta ink (Type 1) Dispersion 120 121 122 123 26 Dispersion method (US: ultrasonic dispersion method PLM PLM PLM PLM PLM PLM PLM: kneading method) Composition Magenta pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Super Super Super Super Super Super Magenta RY Magenta RY Magenta RY Magenta RY Magenta RY Magenta RY (parts) (solid content) 8 6 6 6 6 6 Anionic Name/Product name Resin A Resin A Resin A Resin A Resin A Resin A group-containing (parts) (solid content) 1.6 1.2 1.2 1.2 1.2 1.2 organic polymer Name/Product name — — CMC DN-100L CMC — compound 1390 1390 (parts) (solid content) — — 0.15 0.225 0.15 — Bio-nanofiber Product name CEL-KY CEL-KY CEL-NF CHI-NF CHI-NF — (abbreviation) (parts) (solid content) 0.2 0.15 0.15 0.3 0.225 — Triethylene glycol (parts) 5.4 4.05 4.05 4.05 4.05 4.05 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 10.3 10.0 10.0 10.1 9.8 10.0 properties Average particle diameter D50/nm 101 96 98 88 91 101 Initial viscosity (mPa · s) — 47.8 27.6 9.5 5.0 1.5 Optical density Measured value — 1.16 1.17 1.20 1.19 1.12 Improvement rate — 104% 104% 107% 106% (Reference) Determination — G G G G — Rubfastness — G G G G N

TABLE 21 Compara- Compara- tive tive Comparative Example Example Example Example Example Example Example Aqueous magenta ink (Type 1) 124 125 126 127 27 28 29 Dispersion method (US: ultrasonic dispersion method Self- Self- Self- Self- Self- Self- Self- PLM: kneading method) dispersion dispersion dispersion dispersion dispersion dispersion dispersion type type type type type type type Composition Magenta pigment Product name CAB- CAB- CAB- CAB- CAB- CAB- CAB-O-JET O-JET O-JET O-JET O-JET O-JET O-JET 465M 465M 465M 465M 465M 465M 465M (parts) (solid content) 6 6 6 6 6 6 6 Anionic group-containing Name/Product name — — — — — — — organic polymer (parts) (solid content) — — — — — — — compound Name/Product name CMC DN-800H CMC DN-800H DN-800H — — 1390 1390 (parts) (solid content) 0.3 0.3 0.3 0.3 0.3 — — Bio-nanofiber Product name CEL-NF CEL-NF CEL-KY CEL-KY — CEL-NF — (abbreviation) (parts) (solid content) 0.3 0.3 0.3 0.3 — 0.75 — Triethylene glycol (parts) 1.5 1.5 1.5 1.5 1.5 1.5 1.5 Pure water Balance Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 100 Physical pH 9.5 9.3 9.7 9.7 9.5 10.0 9.7 properties Average particle diameter D50/nm 74 69 75 71 84 193 73 Initial viscosity (mPa · s) 24.1 18.2 20.9 16.5 5.5 158.0 2.4 Optical density Measured value 1.37 1.31 1.16 1.15 1.10 1.65 1.08 Improvement rate 127% 121% 107% 106% 101% 152% (Reference) Determination G G G G N G — Rubfastness G G G G N N N

TABLE 22 Production Example 3 US Example Example Example Example Aqueous magenta ink (Type 2) Dispersion 128 129 130 131 Dispersion method (US: ultrasonic dispersion method) US US US US US Composition Magenta pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Super Super Super Super Super Magenta RY Magenta RY Magenta RY Magenta RY Magenta RY (parts) (solid content) 8 4 4 4 4 Anionic: group- Name/Product name SA-1 SA-1 SA-1 SA-1 SA-1 containing organic (parts) (solid content)   2.4   1.2   1.2   1.2   1.2 polymer compound Name/Product name — — — — CMC1390 (parts) (solid content) — — — —   0.2 Bio-nanofiber Product name CHI-NF CHI-NF CEL-KY CEL-KY CEL-KY (abbreviation) (parts) (solid content)   0.1   0.05   0.2   0.1   0.1 2-Pyrrolidone (parts) — 8 8 8 8 Triethylene glycol — 8 8 8 8 Glycerin (parts) — 3 3 3 3 Triethylene glycol (parts) 8 4 4 4 4 Surfynol 440 (parts) —   0.5   0.5   0.5   0.5 Pure water Balance Balance Balance Balance Balance Total (parts) 100  100  100  100  100  Physical pH   9.9   8.8   9.0   9.1   9.2 properties Average particle diameter D50/nm 96  95  102  110  110  Initial viscosity (mPa · s) —   3.3  16.2  10.9  13.2 Optical density Measured value —   0.91   0.97   0.96   0.98 Improvement rate — 105% 111% 110% 113% Determination — G G G G Rubfastness — G G G G Ink jet adaptability — G M G G Example Example Example Example Example Aqueous magenta ink (Type 2) 132 133 134 135 136 Dispersion method (US: ultrasonic dispersion method) US US US US US Composition Magenta pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Super Super Super Super Super Magenta RY Magenta RY Magenta RY Magenta RY Magenta RY (parts) (solid content) 4 4 4 4 4 Anionic: group- Name/Product name SA-1 SA-1 SA-1 SA-1 SA-1 containing organic (parts) (solid content)   1.2   1.2   1.2   1.2   1.2 polymer compound Name/Product name DN-800H — DN-800H DN-100L DN-10L (parts) (solid content)   0.2 —   0.15   0.2   0.1 Bio-nanofiber Product name CEL-KY CHI-NF CHI-NF CHI-NF CHI-NF (abbreviation) (parts) (solid content)   0.1   0.15   0.15   0.2   0.2 2-Pyrrolidone (parts) 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 Triethylene glycol (parts) 4 4 4 4 4 Surfynol 440 (parts)   0.5   0.5   0.5   0.5   0.5 Pure water Balance Balance Balance Balance Balance Total (parts) 100  100  100  100  100  Physical pH   9.2   8.8   9.2   9.3   9.0 properties Average particle diameter D50/nm 109  95  92  93  95  Initial viscosity (mPa · s)   9.8  16.1   9.1   9.3   7.2 Optical density Measured value   0.98   0.92   0.92   0.94   0.91 Improvement rate 113% 106% 106% 108% 105% Determination G G G G G Rubfastness G G G G G Ink jet adaptability G M G G G

TABLE 23 Comparative Example Example Example Example Example Aqueous magenta ink (Type 2) 137 138 30 139 140 Dispersion method (US: ultrasonic dispersion method) US US US US US Composition Magenta pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Super Super Super Super Super Magenta RY Magenta RY Magenta RY Magenta RY Magenta RY (parts) (solid content) 4 4 4 4 4 Anionic group- Name/Product name SA-1 SA-1 SA-1 UR-1 UR-1 containing organic (parts) (solid content)   1.2   1.2   1.2   1.2   1.2 polymer compound Name/Product name DN-100L DN-800H — — — (parts) (solid content)   0.15   0.15 — — — Bio-nanofiber Product name CHI-NF CHI-NF — CEL-KY CHI-NF (abbreviation) (parts) (solid content)   0.25   0.4 —   0.1   0.15 2-Pyrrolidone (parts) 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 Triethylene glycol (parts) 4 4 4 4 4 Surfynol 440 (parts)   0.5   0.5   0.5   0.5   0.5 Pure water Balance Balance Balance Balance Balance Total (parts) 100  100  100  100  100  Physical pH   8.8   9.0   9.3   8.0   8.4 properties Average particle diameter D50/nm 95  99  109  108  102  Initial viscosity (mPa · s)  17.8  18.5   2.3  12.2   7.7 Optical density Measured value   0.92   0.98   0.87   0.90   0.87 Improvement rate 106% 113% (Reference) 111% 107% Determination G G — G G Rubfastness G G N G G Ink jet adaptability M M G G G Comparative Example Example Example Example Example Aqueous magenta ink (Type 2) 141 142 143 144 31 Dispersion method (US: ultrasonic dispersion method) US US US US US Composition Magenta pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Super Super Super Super Super Magenta RY Magenta RY Magenta RY Magenta RY Magenta RY (parts) (solid content) 4 4 4 4 4 Anionic group- Name/Product name UR-1 UR-1 UR-1 UR-1 UR-1 containing organic (parts) (solid content)   1.2   1.2   1.2   1.2   1.2 polymer compound Name/Product name DN-800H DN-10L CMC DN-100L — 1390 (parts) (solid content)   0.15   0.1   0.2   0.15 — Bio-nanofiber Product name CHI-NF CHI-NF CHI-NF CHI-NF — (abbreviation) (parts) (solid content)   0.15   0.15   0.1   0.4 — 2-Pyrrolidone (parts) 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 Triethylene glycol (parts) 4 4 4 4 4 Surfynol 440 (parts)   0.5   0.5   0.5   0.5   0.5 Pure water Balance Balance Balance Balance Balance Total (parts) 100  100  100  100  100  Physical pH   8.1   8.5   7.4   8.4   7.9 properties Average particle diameter D50/nm 107  101  102  108  110  Initial viscosity (mPa · s)   9.3 9   7.8  18.2   2.9 Optical density Measured value   0.87   0.88   0.85   0.90   0.81 Improvement rate 107% 109% 105% 111% (Reference) Determination G G G G — Rubfastness G G G G N Ink jet adaptability G G G M G

TABLE 24 Production Example 7 PLM Example Example Example Example Aqueous magenta ink (Type 2) Dispersion 145 146 147 148 Dispersion method (US: ultrasonic dispersion method PLM PLM PLM PLM PLM PLM: kneading method) Composition Magenta pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Super Super Super Super Super Magenta RY Magenta RY Magenta RY Magenta RY Magenta RY (parts) (solid content) 8 4 4 4 4 Anionic group- Name/Product name Resin A Resin A Resin A Resin A Resin A containing organic (parts) (solid content) 1.6 0.8 0.8 0.8 0.8 polymer compound Name/Product name — — — CMC — 1390 (parts) (solid content) — — — 0.1 — Bio-nanofiber Product name CEL-KY CEL-KY CEL-KY CEL-KY CHI-NF (abbreviation) (parts) (solid content) 0.2 0.1 0.2 0.1 0.15 2-Pyrrolidone (parts) — 8 8 8 8 Triethylene glycol — 8 8 8 8 Glycerin (parts) — 3 3 3 3 Triethylene glycol (parts) 5.4 2.7 2.7 2.7 2.7 Surfynol 440 (parts) — 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical pH 10.3 9.2 9.2 9.2 8.8 properties Average particle diameter D50/nm 101 101 104 103 96 Initial viscosity (mPa · s) — 3.8 8.8 18.9 16.1 Optical density Measured value — 0.88 0.89 0.92 0.88 Improvement rate — 104% 105% 108% 104% Determination — G G G G Rubfastness — G G G G Ink jet adaptability — G G G M Comparative Comparative Example Example Example Example Example Aqueous magenta ink (Type 2) 149 150 151 32 33 Dispersion method (US: ultrasonic dispersion method PLM PLM PLM PLM PLM PLM: kneading method) Composition Magenta pigment Product name FASTOGEN FASTOGEN FASTOGEN FASTOGEN FASTOGEN Super Super Super Super Super Magenta RY Magenta RY Magenta RY Magenta RY Magenta RY (parts) (solid content) 4 4 4 4 4 Anionic group- Name/Product name Resin A Resin A Resin A Resin A Resin A containing organic (parts) (solid content) 0.8 0.8 0.8 0.8 0.8 polymer compound Name/Product name DN-800H DN-100L CMC CMC — 1390 1390 (parts) (solid content) 0.15 0.15 0.1 0.1 — Bio-nanofiber Product name CHI-NF CHI-NF CHI-NF — — (abbreviation) (parts) (solid content) 0.1 0.2 0.15 — — 2-Pyrrolidone (parts) 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 Triethylene glycol (parts) 2.7 2.7 2.7 2.7 2.7 Surfynol 440 (parts) 05 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical pH 9.2 9.3 9.0 9.2 9.2 properties Average particle diameter D50/nm 92 93 96 106 106 Initial viscosity (mPa · s) 9.8 11.3 8.8 9.9 2.6 Optical density Measured value 0.88 0.91 0.90 0.86 0.85 Improvement rate 104% 107% 106% 101% (Reference) Determination G G G N — Rubfastness G G G N N Ink jet adaptability G M G G G

TABLE 25 Comparative Comparative Comparative Example Example Example Example Example Example Example Aqueous magenta ink (Type 2) 152 153 154 155 34 35 36 Dispersion method (US: ultrasonic dispersion method Self- Self- Self- Self- Self- Self- Self- PLM: kneading method) dispersion dispersion dispersion dispersion dispersion dispersion dispersion type type type type type type type Composition Magenta pigment Product name CAB-O- CAB-O- CAB-O- CAB-O- CAB-O- CAB-O- CAB-O- JET JET JET JET JET JET JET 465M 465M 465M 465M 465M 465M 465M (parts) (solid content) 4 4 4 4 4 4 4 Anionic group- Name/Product name — — — — — — — containing organic (parts) (solid content) — — — — — — — polymer compound Name/Product name CMC DN-800H CMC DN-800H — CMC — 1390 1390 1390 (parts) (solid content) 0.2 0.2 0.2 0.2 — 0.2 — Bio-nanofiber Product name CEL-NF CEL-NF CEL-KY CEL-KY CEL-KY — — (abbreviation) (parts) (solid content) 0.2 0.2 0.2 0.2 0.5 — — 2-Pyrrolidone (parts) 8 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 3 Triethylene glycol (parts) 1 1 1 1 1 1 1 Surfynol 440 (parts) 0.5 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 100 Physical pH 8.7 8.5 8.9 8.9 9.1 9.0 8.9 properties Average particle diameter D50/nm 78 73 79 75 98 86 77 Initial viscosity (mPa · s) 13 9.3 11.5 8.8 298 6.9 2 Optical density Measured value 0.99 0.96 0.88 0.87 1.34 0.84 0.82 Improvement rate 121% 117% 107% 106% 163% 102% (Reference) Determination G G G G G N — Rubfastness G G G G G N N Ink jet adaptability G G G G N G G

TABLE 26 Production Example 4 US Example Example Example Example Aqueous yellow ink (Type 1) Dispersion 156 157 158 159 Dispersion method (US: ultrasonic dispersion method US US US US US PLM: kneading method) Composition Yellow pigment Product name Fast Yellow Fast Yellow Fast Yellow Fast Yellow Fast Yellow 7413 7413 7413 7413 7413 (parts) (solid content) 8 6 6 6 6 Anionic group- Name/Product name SA-1 SA-1 SA-1 SA-1 SA-1 containing organic (parts) (solid content) 1.6 1.2 1.2 1.2 1.2 polymer compound Name/Product name — — — CMC DN-800H 1390 (parts) (solid content) — — — 0.15 0.3 Bio-nanofiber Product name CEL-NF CEL-NF CEL-KY CEL-NF CEL-NF (abbreviation) (parts) (solid content) 0.4 0.3 0.3 0.15 0.3 Triethylene glycol (parts) 8 6 6 6 6 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical pH 9.9 9.9 9.8 9.8 9.5 properties Average particle diameter D50/nm 99 99 87 104 102 Initial viscosity (mPa · s) — 17.7 30.1 51.1 72.2 Optical density Measured value — 1.30 1.22 1.36 1.34 Improvement rate — 111% 104% 116% 114% Determination — G G G G Rubfastness — G G G G Comparative Example Example Example Example Example Aqueous yellow ink (Type 1) 160 161 167 163 37 Dispersion method (US: ultrasonic dispersion method US US US US US PLM: kneading method) Composition Yellow pigment Product name Fast Yellow Fast Yellow Fast Yellow Fast Yellow Fast Yellow 7413 7413 7413 7413 7413 (parts) (solid content) 6 6 6 6 6 Anionic group- Name/Product name SA-1 SA-1 SA-1 SA-1 SA-1 containing organic (parts) (solid content) 1.2 1.2 1.2 1.2 1.2 polymer compound Name/Product name — — DN-800H DN-800H — (parts) (solid content) — — 0.15 0.3 — Bio-nanofiber Product name CHI-NF CHI-NF CHI-NF CHI-NF — (abbreviation) (parts) (solid content) 0.075 0.225 0.375 0.45 — Triethylene glycol (parts) 6 6 6 6 6 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical pH 9.6 10.0 9.6 9.8 9.5 properties Average particle diameter D50/nm 96 102 104 102 90 Initial viscosity (mPa · s) 3.4 5.1 14.2 28.9 1.5 Optical density Measured value 1.21 1.29 1.35 1.33 1.17 Improvement rate 103% 110% 115% 113% (Reference) Determination G G G G — Rubfastness G G G G N

TABLE 27 Production Example 8 Comparative PLM Example Example Example Example Example Example Aqueous yellow ink (Type 1) Dispersion 164 165 166 167 168 38 Dispersion method (US: ultrasonic dispersion method PLM PLM PLM PLM PLM PLM PLM PLM: kneading method) Composition Yellow pigment Product name Fast Fast Fast Yellow Fast Fast Yellow Fast Fast Yellow Yellow Yellow 7413 Yellow 7413 Yellow 7413 7413 7413 7413 7413 (parts) (solid content) 8 6 6 6 6 6 6 Anionic group- Name/Product name Resin A Resin A Resin A Resin A Resin A Resin A Resin A containing organic (parts) (solid content) 2.4 1.8 1.8 1.8 1.8 1.8 1.8 polymer compound Name/Product name — — — CMC — DN-800H — 1390 (parts) (solid content) — — — 0.15 — 0.225 — Bio-nanofiber Product name CHI-NF CHI-NF CEL-KY CEL-KY CHI-NF CHI-NF — (abbreviation) (parts) (solid content) 0.1 0.075 0.15 0.15 0.225 0.6 — Triethylene glycol (parts) 4.4 3.3 3.3 3.3 3.3 3.3 3.3 Pure water Balance Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 100 Physical pH 10.1 10.1 10.2 10.1 10.1 10.1 10.1 properties Average particle diameter D50/nm 86 86 62 73 87 89 76 Initial viscosity (mPa · s) — 3.5 149.1 31.2 6.2 23.9 1.6 Optical density Measured value — 1.08 1.10 1.15 1.20 1.22 1.03 Improvement rate — 105% 106% 111% 116% 118% (Reference) Determination — G G G G G — Rubfastness — G G G G G N

TABLE 28 Comparative Comparative Comparative Example Example Example Example Example Example Example Aqueous yellow ink (Type 1) 169 170 171 172 39 40 41 Dispersion method (US: ultrasonic dispersion method Self- Self- Self- Self- Self- Self- Self- PLM: kneading method) dispersion dispersion dispersion dispersion dispersion dispersion dispersion type type type type type type type Composition Yellow pigment Product name CAB-O- CAB-O- CAB-O- CAB-O- CAB-O-JET CAB-O-JET CAB-O-JET JET JET JET JET 470Y 470Y 470Y 470Y 470Y 470Y 470Y (parts) (solid content) 6 6 6 6 6 6 6 Anionic group- Name/Product name — — — — — — — containing organic (parts) (solid content) — — — — — — — polymer compound Name/Product name CMC DN-800H CMC DN-800H CMC — — 1390 1390 1390 (parts) (solid content) 0.3 0.3 0.3 0.3 0.3 — — Bio-nanofiber Product name CEL-NF CEL-NF CEL-KY CEL-KY — CEL-NF — (abbreviation) (parts) (solid content) 0.3 0.3 0.3 0.3 — 0.75 — Triethylene glycol (parts) 1.5 1.5 1.5 1.5 1.5 1.5 1.5 Pure water Balance Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 100 Physical pH 8.9 8.8 9.0 8.9 9.9 10.1 9.0 properties Average particle diameter D50/nm 132 137 126 123 80 189 113 Initial viscosity (mPa · s) 14.2 9.3 11.8 8.1 3.9 611 1.2 Optical density Measured value 1.22 1.19 1.10 1.07 1.05 1.58 1.03 Improvement rate 118% 116% 107% 105% 102% 153% (Reference) Determination G G G G N G — Rubfastness G G G G N N N

TABLE 29 Production Example 4 US Example Example Example Example Example Aqueous yellow ink (Type 2) Dispersion 173 174 175 176 177 Dispersion method (US: ultrasonic dispersion US US US US US US method PLM: kneading method) Composition Yellow Product name Fast Yellow Fast Yellow Fast Yellow Fast Yellow Fast Yellow Fast Yellow pigment 7413 7413 7413 7413 7413 7413 (parts) (solid content) 8 4 4 4 4 4 Anionic Name/Product name SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 group- (parts) (solid content) 1.6 0.8 0.8 0.8 0.8 0.8 containing Name/Product name — — — — CMC DN-800H organic 1390 polymer (parts) (solid content) — — — — 0.1 0.1 compound Bio- Product name CEL-NF CEL-NF CEL-KY CEL-KY CEL-KY CEL-KY nanofiber (abbreviation) (parts) (solid content) 0.4 0.2 0.2 0.1 0.1 0.1 2-Pyrrolidone (parts) — 8 8 8 8 8 Triethylene glycol — 8 8 8 8 8 Glycerin (parts) — 3 3 3 3 3 Triethylene glycol (parts) 8 4 4 4 4 4 Surfynol 440 (parts) — 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 9.9 9.0 8.9 9.2 8.9 8.6 properties Average particle diameter D50/nm 99 106 94 110 112 120 Initial viscosity (mPa · s) — 2.7 18.7 10.8 19.5 17.6 Optical Measured value — 1.07 1.01 1.00 1.03 1.04 density Improvement rate — 110% 104% 103% 106% 107% Determination — G G G G G Rubfastness — G G G G G Ink jet adaptability — G M G M M Example Example Example Example Example Example Aqueous yellow ink (Type 2) 178 179 180 181 182 183 Dispersion method (US: ultrasonic dispersion US US US US US US method PLM: kneading method) Composition Yellow Product name Fast Yellow Fast Yellow Fast Yellow Fast Yellow Fast Yellow Fast Yellow pigment 7413 7413 7413 7413 7413 7413 (parts) (solid content) 4 4 4 4 4 4 Anionic Name/Product name SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 group- (parts) (solid content) 0.8 0.8 0.8 0.8 0.8 0.8 containing Name/Product name DN-10L CMC DN-800H DN-10L — — organic 1390 polymer (parts) (solid content) 0.1 0.2 0.2 0.2 — — compound Bio- Product name CEL-KY CEL-NF CEL-NF CEL-NF CHI-NF CHI-NF nanofiber (abbreviation) (parts) (solid content) 0.1 0.2 0.7 0.2 0.05 0.15 2-Pyrrolidone (parts) 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 Triethylene glycol (parts) 4 4 4 4 4 4 Surfynol 440 (parts) 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 8.8 8.8 8.6 8.8 8.7 9.1 properties Average particle diameter D50/nm 119 109 110 133 103 110 Initial viscosity (mPa · s) 11.2 5.4 2.7 19.9 3.6 11.8 Optical Measured value 1.05 1.10 1.10 1.08 1.00 1.06 density Improvement rate 108% 113% 113% 111% 103% 109% Determination G G G G G G Rubfastness G G G G G G Ink jet adaptability G G G M G G

TABLE 30 Comparative Example Example Example Example Example Example Example Aqueous yellow ink (Type 2) 184 185 186 187 188 189 42 Dispersion method (US: ultrasonic dispersion method US US US US US US US PLM: kneading method) Composition Yellow pigment Product name Fast Fast Fast Fast Fast Fast Fast Yellow Yellow Yellow Yellow Yellow Yellow Yellow 7413 7413 7413 7413 7413 7413 7413 (parts) (solid content) 4 4 4 4 4 4 4 Anionic group-containing Name/Product name SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 SA-1 organic polymer (parts) (solid content) 0.8 0.8 0.8 0.8 0.8 0.8 0.8 compound Name/Product name DN-800H CMC DN-100L DN-10L DN-800H DN-800H — 1390 (parts) (solid content) 0.1 0.1 0.15 0.2 0.1 0.2 — Bio-nanofiber Product name CHI-NF CHI-NF CHI-NF CHI-NF CHI-NF CHI-NF — (abbreviation) (parts) (solid content) 0.15 0.15 0.15 0.1 0.25 0.3 — 2-Pyrrolidone (parts) 8 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 3 Triethylene glycol (parts) 4 4 4 4 4 4 4 Surfynol 440 (parts) 0.5 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 100 Physical pH 8.9 9.0 8.7 8.6 8.7 8.9 8.6 properties Average particle diameter D50/nm 111 113 108 106 101 110 97 Initial viscosity (mPa · s) 5.5 18.9 5.1 11.2 19.8 12.5 2.8 Optical density Measured value 1.01 1.03 1.03 1.03 1.09 1.05 0.97 Improvement rate 104% 106% 106% 106% 112% 108% (Reference) Determination G G G G G G — Rubfastness G G G G G G G Ink jet adaptability G M G G M G G

TABLE 31 Production Example 8 PLM Example Example Example Example Example Aqueous yellow ink (Type 2) Dispersion 190 191 192 193 194 Dispersion method (US: ultrasonic dispersion method PLM PLM PLM PLM PLM PLM PLM: kneading method) Composition Yellow pigment Product name Fast Fast Fast Fast Fast Fast Yellow Yellow Yellow Yellow Yellow Yellow 7413 7413 7413 7413 7413 7413 (parts) (solid content) 8 4 4 4 4 4 Anionic group- Name/Product name Resin A Resin A Resin A Resin A Resin A Resin A containing organic (parts) (solid content) 2.4 1.2 1.2 1.2 1.2 1.2 polymer compound Name/Product name — — — — CMC — 1390 (parts) (solid content) — — — — 0.1 — Bio-nanofiber Product name CHI-NF CHI-NF CEL-KY CEL-KY CEL-KY CHI-NF (abbreviation) (parts) (solid content) 0.1 0.05 0.2 0.1 0.1 0.15 2-Pyrrolidone (parts) — 8 8 8 8 8 Triethylene glycol — 8 8 8 8 8 Glycerin (parts) — 3 3 3 3 3 Triethylene glycol (parts) 4.4 2.2 2.2 2.2 2.2 2.2 Surfynol 440 (parts) — 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 10.1 9.2 9.3 9.3 9.2 9.2 properties Average particle diameter D50/nm 86 82 78 67 79 82 Initial viscosity (mPa · s) — 3.1 15.6 4.3 19.6 16.1 Optical density Measured value — 0.90 0.92 0.91 0.95 0.99 Improvement rate — 105% 107% 106% 110% 115% Determination — G G G G G Rubfastness — G G G G G Ink jet adaptability — G G G M M Example Example Example Example Example Example Aqueous yellow ink (Type 2) 195 196 197 198 199 200 Dispersion method (US: ultrasonic dispersion method PLM PLM PLM PLM PLM PLM PLM: kneading method) Composition Yellow pigment Product name Fast Fast Fast Fast Fast Fast Yellow Yellow Yellow Yellow Yellow Yellow 7413 7413 7413 7413 7413 7413 (parts) (solid content) 4 4 4 4 4 4 Anionic group- Name/Product name Resin A Resin A Resin A Resin A Resin A Resin A containing organic (parts) (solid content) 1.2 1.2 1.2 1.2 1.2 1.2 polymer compound Name/Product name DN-800H CMC DN-100L DN-10L DN-800H DN-800H 1390 (parts) (solid content) 0.15 0.1 0.15 0.2 0.1 0.15 Bio-nanofiber Product name CHI-NF CHI-NF CHI-NF CHI-NF CHI-NF CHI-NF (abbreviation) (parts) (solid content) 0.15 0.15 0.15 0.1 0.25 0.4 2-Pyrrolidone (parts) 8 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 3 Triethylene glycol (parts) 2.2 2.2 2.2 2.2 2.2 2.2 Surfynol 440 (parts) 0.5 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 100 Physical pH 9.2 9.2 9.2 9.2 9.2 9.2 properties Average particle diameter D50/nm 82 82 82 82 82 85 Initial viscosity (mPa · s) 8.4 10.9 8.8 7.2 9.9 17.9 Optical density Measured value 0.91 0.92 0.96 0.94 0.99 1.01 Improvement rate 106% 107% 112% 109% 115% 117% Determination G G G G G G Rubfastness G G G G G G Ink jet adaptability G G G G G M

TABLE 32 Comparative Comparative Example Example Example Example Example Aqueous yellow ink (Type 2) 43 44 201 202 203 Dispersion method (US: ultrasonic dispersion method PLM PLM Self-dispersion Self-dispersion Self-dispersion PLM: kneading method) type type type Composition Yellow pigment Product name Fast Yellow Fast Yellow CAB-O-JET CAB-O-JET CAB-O-JET 7413 7413 470Y 470Y 470Y (parts) (solid content) 4 4 4 4 4 Anionic group- Name/Product name Resin A Resin A — — — containing organic (parts) (solid content) 1.2 1.2 — — — polymer compound Name/Product name CMC — CMC DN-800H CMC 1390 1390 1390 (parts) (solid content) 0.1 — 0.2 0.2 0.2 Bio-nanofiber Product name — — CEL-NF CEL-NF CEL-KY (abbreviation) (parts) (solid content) — — 0.2 0.2 0.2 2-Pyrrolidone (parts) 8 8 8 8 8 Triethylene glycol 8 8 8 8 8 Glycerin (parts) 3 3 3 3 3 Triethylene glycol (parts) 2.2 2.2 1 1 1 Surfynol 440 (parts) 0.5 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Balance Total (parts) 100 100 100 100 100 Physical pH 9.2 9.2 8.1 8.0 8.2 properties Average particle diameter D50/nm 82 82 142 147 135 Initial viscosity (mPa · s) 10.2 2.7 13.2 11.2 10.9 Optical density Measured value 0.87 0.86 1.09 1.07 0.99 Improvement rate 101% (Reference) 117% 118% 109% Determination N — G G G Rubfastness N N G G G Ink jet adaptability G G G G G Comparative Comparative Comparative Example Example Example Example Aqueous yellow ink (Type 2) 204 45 46 47 Dispersion method (US: ultrasonic dispersion method Self-dispersion Self-dispersion Self-dispersion Self-dispersion PLM: kneading method) type type type type Composition Yellow pigment Product name CAB-O-JET CAB-O-JET CAB-O-JET CAB-O-JET 470Y 470Y 470Y 470Y (parts) (solid content) 4 4 4 4 Anionic group- Name/Product name — — — — containing organic (parts) (solid content) — — — — polymer compound Name/Product name DN-800H — DN-800H — (parts) (solid content) 0.2 — 0.2 — Bio-nanofiber Product name CEL-KY CEL-NF — — (abbreviation) (parts) (solid content) 0.2 0.5 — — 2-Pyrrolidone (parts) 8 8 8 8 Triethylene glycol 8 8 8 8 Glycerin (parts) 3 3 3 3 Triethylene glycol (parts) 1 1 1 1 Surfynol 440 (parts) 0.5 0.5 0.5 0.5 Pure water Balance Balance Balance Balance Total (parts) 100 100 100 100 Physical pH 8.1 9.2 8.7 8.2 properties Average particle diameter D50/nm 132 203 88 121 Initial viscosity (mPa · s) 9.2 456.0 5.5 2.0 Optical density Measured value 0.97 1.40 0.94 0.93 Improvement rate 107% 154% 103% ( 

 ) Determination G G N — Rubfastness G G N N Ink jet adaptability G N G G

The results indicate that an aqueous ink of each color using an aqueous pigment dispersion containing an anionic group-containing organic polymer compound and bio-nanofibers having an average diameter of 1 nm or more and 100 nm or less and an aspect ratio of 100 or more is excellent in optical density, rubfastness, etc. of resultant images. 

1. An aqueous pigment dispersion comprising a pigment, an anionic group-containing organic polymer compound, and bio-nanofibers having an average diameter of 1 nm or more and 100 nm or less and an aspect ratio of 100 or more.
 2. The aqueous pigment dispersion according to claim 1, wherein the bio-nanofibers are cellulose nanofibers or chitosan nanofibers.
 3. The aqueous pigment dispersion according to claim 1, wherein the anionic group-containing organic polymer compound is at least one selected from the group consisting of acrylic resins having anionic groups, polyurethane resins having anionic groups, and polysaccharide derivatives having anionic groups.
 4. The aqueous pigment dispersion according to claim 1, wherein the content of the bio-nanofibers is a bio-nanofibers/pigment ratio of 1/100 to 1/8.